1) delaminate wear
剥层磨损
1.
The results showed that electroless Ni-P coating appear mainly delaminate wear and lightiy abrasive wear under unlubricated wear.
结果表明：化学镀Ni-P合金在无润滑磨损条件下的磨损机理主要为剥层磨损，并伴随少量磨粒磨损。
2) delamination
剥层
1.
Under low impact cycles,the forms of damage are mainly plastic deformation and plastic accumulation;but for high impact cycles,surface crush and delamination occurs because of the plastic exhaustion of the central zone of impact wear scar,and the thick.
结果表明在本试验条件下,磨损体积损失随冲击次数的增加呈非线性增大;在低循环次数下,冲击磨损损伤形式主要为塑性变形及塑性堆积;当循环次数较高时,冲击坑中心由于塑性耗竭而出现表面压碎及剥层磨损,且由激光显微镜测得的剥层厚度在0。
3) layer peeled off analysis
剥层分析
1.
It is confirmed by the layer peeled off analysis that th.
剥层分析表明石墨呈薄层结构平铺在试样观察表面上,而其内部无石墨析出。
4) inside stripping layer method
内剥层法
1.
The tests of inside stripping layer method are conducted on the cold simulation rolls whose types,sizes,material,working and treating methods are different.
求出了原辊和打中心孔或扩孔后辊内残余应力分布曲线；提出了虚拟打孔法和虚拟剥层法，解决了实心辊中心和空心辊内表层的残余应力的精确测量问题，丰富了Ｓａｃｈｓ内剥层法的内容；机械法打中心孔、热处理前打中心孔、空心辊表淬前改变温度场的方法可降低残余应力值，后者降低残余应力的效果尤为显著。
5) exfoliation corrosion
剥层腐蚀
1.
Microstructures of 7475 and 7050 aluminium alloy after different ageing treatments have been investigated by TEM, and normal mechanical properties, fracture toughness and exfoliation corrosion resistance have been tested as well.
利用透射电子显微镜分析了7475和7050铝合金经不同时效制度处理后的显微组织,并测试了不同状态下合金的常规力学性能及部分断裂韧性和合金的抗剥层腐蚀能力。
6) peel measurement
剥层测定
参考词条
补充资料：剥层腐蚀
分子式：
CAS号：
性质：金属材料晶间腐蚀的一种类型。腐蚀优先沿晶界向内部发展，致使晶界丧失力学性能，金属表层沿晶界发生逐层剥落。主要发生于铝合金中，是航空用铝合金腐蚀失效的主要类型，可采用表面保护涂层的方法进行防护。
CAS号：
性质：金属材料晶间腐蚀的一种类型。腐蚀优先沿晶界向内部发展，致使晶界丧失力学性能，金属表层沿晶界发生逐层剥落。主要发生于铝合金中，是航空用铝合金腐蚀失效的主要类型，可采用表面保护涂层的方法进行防护。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。