1) grain subdivision
亚晶化
2) subgrain strengthening
亚晶强化
3) Subgrain stabilizing treatment
亚晶稳定化
4) sublattice magnetization
亚晶格磁化
5) subgrain
亚晶
1.
After one ECAP deformation pass,profuse subgrains with the size of 650900nm are formed,few dislocations can be found inside the subgrains,but high density dislocation networks still are observed in some grains,the hardness of material increases 87%.
组织和性能检测表明:在连续ECAP变形一道次后,在晶粒内部形成了直径为650~900 nm且内部基本无位错的亚晶,但部分大晶粒内部仍存在高密度的位错网,材料硬度提高了87%;经过4道次连续ECAP变形后,亚晶并未进一步细化,但亚晶界趋于平直、清晰,且亚晶内部基本未见位错组织,材料硬度提高也不显著;与传统ECAP相比,连续ECAP工艺由于具有较高的变形区温度,促进了晶内位错的反应即动态回复过程,较早形成了平直清晰的亚晶结构,同时伴随每道次变形过程的动态回复也降低了最后晶格中累积的能量,使变形两道次后的组织和性能变化不显著。
2.
The results show that the subgrain structures of the ferrite-strip along the drawing direction are formed in the deformation bands of steel.
结果表明:在变形带中,铁素体沿平行于剪切应力方向形成条带状亚晶, {110}晶面为变形条带状亚晶的滑移面,条带状亚晶内存在高密度位错;经退火处理后,条带状亚晶内的位错束集成与条带状亚晶界垂直的位错胞壁,形成类方形位错胞结构;进一步经位错胞壁的扩散迁移,形成各胞壁之间呈120°夹角的亚晶结构。
3.
Semi-empirical relations between subgrain sizes and deformation variables were construct.
利用 ＴＥＭ分析了合金在不同压缩条件下的组织形貌特征，采用ＥＢＳＰ分析了晶粒间的取向差，研究了其动态再结晶行为通过回归分析建立了７００５合金热变形条件与变形亚晶尺寸间关系的半经验模型。
6) sub-grain
亚晶
1.
At higher drawing strains,a single fiber was divided into sub-grains.
在较低的应变量下纤维保持着与铸态树枝晶相同的bcc单晶结构,在较高的应变量下,单根Cr纤维被分隔为一些由亚晶界组成的亚结构,相邻亚晶的偏差角在5~30°之间。
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。