1) elastic flexure differenti-cal equatio
弹性弯曲方程
2) bending elasticity
弯曲弹性
1.
Comparison of bending elasticity of hollow PET fiber;
不同中空涤纶弯曲弹性比较
4) bent-up construction
弹性曲弯
5) elastic-plastic bending
弹塑性弯曲
1.
In order to make a thorough and precise study in the roller leveling process,a 3D axisymmetric elastic-plastic bending mathematical model of plate based on the Prandtle-Reuss increment theory was given,according to the relevant initial conditions and boundary conditions of plate and leveler.
为了完整和精确地计算辊式矫直过程,根据钢板和矫直机相应的初始条件和边界条件,采用曲率变化量积分的方法,建立了基于Prandtle-Reuss增量理论的三维弹塑性弯曲解析数学模型。
6) flexural resilience
弯曲回弹性
1.
Moreover, PET\|PBT fiber exhibits 180° flexural resilience higher than that of PET or PBT fiber and matching with that of PA6 fiber, and shows dyeing behavior far better than that of PET fiber.
PET-PBT纤维的 180°弯曲回弹性能高于 PET,PBT纤维 ,和 PA6纤维相当。
补充资料：弯曲工艺的概念及弯曲件
1．弯曲工艺：是根据零件形状的需要，通过模具和压力机把毛坯弯成一定角度，一定形状工件的冲压工艺方法。
2．弯曲成形工艺在工业生产中的应用：应用相当广泛，如汽车上很多履盖件，小汽车的柜架构件，摩托车上把柄，脚支架，单车上的支架构件，把柄，小的如门扣，夹子（铁夹）等。
弯曲的基本原理：以V形板料弯曲件的弯曲变形为例进行说明。其过程为：
1． 凸模运动接触板料（毛坯）由于凸,凹模不同的接触点力作用而产生弯矩， 在弯矩作用下发生弹性变形，产生弯曲。
2． 随着凸模继续下行，毛坯与凹模表面逐渐靠近接触，使弯曲半径及弯曲力臂均随之减少，毛坯与凹模接触点由凹模两肩移到凹模两斜面上。（塑变开始阶段）。
3．随着凸模的继续下行，毛坯两端接触凸模斜面开始弯曲。（回弯曲阶段）。
4．压平阶段，随着凸凹模间的间隙不断变小，板料在凸凹模间被压平。
5． 校正阶段，当行程终了，对板料进行校正，使其圆角直边与凸模全部贴合而成所需的形状。
弯曲变形的特点： 弯曲变形的特点是：板料在弯曲变形区内的曲率发生变化，即
弯 曲半径发生变化。从弯曲断面可划分为三个区：拉伸区、压缩区和中性层。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。