1) inside explosive loading
内爆炸加载
2) explosive loading
爆炸加载
1.
Fragmentation behavior of tungsten heavy alloys under explosive loading;
爆炸加载条件下高密度钨合金破碎性的实验研究
2.
Fragment distribution of tungsten alloy under explosive loading;
爆炸加载下钨合金破片分布的试验研究
3.
The fracture morphology and microstructure of Uranium-Niobium caused by explosive loading were investigated.
结果表明:U-Nb合金在爆炸加载下的断裂方式为剪切断裂;破片组织内部发现因高速应变引起的大量的绝热剪切带,靠近绝热剪切带的基体晶粒发生明显的拉长变形;破片中存在大量的微裂纹,裂纹沿着绝热剪切带扩展,当与沿壳体环向的拉应力形成的纵向主裂纹相交汇时,形成破片。
3) blasting loading
爆炸加载
1.
This paper establishes the experimental system of rock s constitutive relation under blasting loading and indicates that the planewave producer is a suitable method to study rock s constitutive relation in ordinary blasting laboratory.
建立了爆炸加载条件下岩石动态本构关系的实验和量测系统，通过研究认为平面波发生器是更适合于作为一般爆破实验室研究动态本构关系的手段。
5) inside-explosive loading
内爆炸载荷
6) implosion loading
内爆加载
1.
and analysising the dynamic fracture, the damage function model is implemented in 2D finite element code—DEFEL, with which the spallation under impact loading and the spallation of metal cylinder under implosion loading, are simulated using criterion of critical damage.
为推广和拓展损伤度函数模型的应用范围,探讨用损伤的观点来分析材料的动态断裂问题,本文把损伤度函数模型嵌入到二维流体弹塑性动力有限元编码DEFEL中,使之与原编码的力学计算耦合,并以临界损伤度作为断裂准则,对平面撞击层裂过程和滑移爆轰内爆加载下金属柱壳的内聚运动及层裂过程进行了二维数值模拟研究,并结合实验结果,讨论了材料的损伤破坏过程及有关现象。