1) epoxy coated steel bars
环氧涂层钢筋
1.
The flexural behavior of partially prestressed concrete beams with unbonded prestressing CFRP tendons and epoxy coated steel bars is investigated,and the full-range tests are loaded for 8 beams until the failure.
研究以碳纤维筋为无粘结预应力筋和环氧涂层钢筋为非预应力筋的部分预应力混凝土梁的受弯性能。
2) epoxy resin coated steel bar
环氧树脂涂层钢筋
1.
This article introduces the key constructing points of the epoxy resin coated steel bar to provide reference for engineering.
文章介绍了环氧树脂涂层钢筋施工操作要点,为工程施工提供借鉴。
2.
The corrosion problem of reinforcement of reiforced concrete can be solved with fiber plastic reinforcement and epoxy resin coated steel bar.
纤维塑料筋及环氧树脂涂层钢筋可以解决钢筋混凝土存在的钢筋锈蚀问题 ,从生产、施工、防腐性、经济性来说都是实用的。
3.
Concerning preparation work before construction and quality control &supervision during construction for epoxy resin coated steel bar in Shantou LPG Wharf,effective requirements on supervision are stipulated and suggestions on problems ealsted inconstruction are put forward.
介绍在汕头LPG码头工程中，对环氧树脂涂层钢筋的施工前准备、施工过程中的质量控制和监督，规定了有效的监理要求，并对施工中存在问题提出处理建议。
3) epoxy resin coated steel bars
环氧树脂涂层钢筋
1.
The cohesive anchorage property of epoxy resin coated steel bars areweakened because of the change in surface condition.
环氧树脂涂层钢筋因表面状态的改变，使粘结锚固性能受到削弱。
4) coated steel
涂层钢筋
1.
The paper introduced the construction technology,scope and attentions of coated steel for popularizing ECS technology.
环氧树脂涂层钢筋(EpoxyCoatedSteel,简称ECS),在我国工程结构因钢筋锈蚀而造成的损失是不可低估的,因此钢筋防锈是一个迫切需要解决的问题。
5) epoxy coating steel strand
环氧涂层钢绞线
1.
In bridge construction, engineers need cables which have higher antisepsis performance and higher strength than before, and the epoxy coating steel strand has above requirements and is used in many projects.
桥梁建设对索体防腐性能及强度要求不断提高 ,环氧涂层钢绞线因符合上述要求而被广泛应用 ,通过介绍宜宾中坝桥采用前支点挂篮及钢绞线斜拉索的施工过程 ,详述环氧涂层钢绞线拉索在斜拉桥中的具体应用。
6) epoxide steel
环氧树脂涂刷钢筋
补充资料：双(2,3-环氧环戊基)醚玻璃布层合板
分子式：
CAS号：
性质：以双(2,3-环氧环戊基)醚为基料的层合板。马丁耐热270℃。拉伸强度371MPa。弯曲强度487MPa。冲击强度125kJ／m2。体积电阻率l.18×1015Ω·cm。将双(2,3-环氧环戊基)醚与固化剂等制成胶液或B阶树脂后,充分浸渍玻璃布,再叠层并层合即得。主要用作航空航天器材、电子元件和体育器材等。
CAS号：
性质：以双(2,3-环氧环戊基)醚为基料的层合板。马丁耐热270℃。拉伸强度371MPa。弯曲强度487MPa。冲击强度125kJ／m2。体积电阻率l.18×1015Ω·cm。将双(2,3-环氧环戊基)醚与固化剂等制成胶液或B阶树脂后,充分浸渍玻璃布,再叠层并层合即得。主要用作航空航天器材、电子元件和体育器材等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。