1) high strength expanded shale
高强页岩陶粒
1.
On the basis of measurement of high strength expanded shale properties, concrete mixtures of ten different proportions with design strength of 20 MPa to 60 MPa were prepared.
在高强页岩陶粒性能测定的基础上,配制了10种不同配合比的混凝土拌和物,其设计强度为20～60MPa。
2.
A new type of asphalt mixture was prepared with high strength expanded shale and was applied successfully to pavement.
采用高强页岩陶粒制备了一种轻质、抗滑、降噪的新型沥青混合料,并将这种沥青混合料成功应用于路面工程。
2) haydite shale
陶粒页岩
1.
The physicochemical properties and technical performance of the haydite shale in the Jiutai-Changchun convex belt;
九台—长春凸起带陶粒页岩的物理化学特征及工艺性能
2.
The effect on the sintering and expanding property of haydite shale;
影响陶粒页岩烧胀性能因素探讨
3.
The geological features of the Huayuan haydite shale deposit, Nong'an, Jilin Province and its origin study;
吉林省农安县花园陶粒页岩矿床地质特征及成因探讨
3) shale ceramsite
页岩陶粒
1.
Study on properties of shale ceramsite concrete;
页岩陶粒混凝土性能的研究
2.
Effect of shale ceramsite on failure character and mechanism of concrete
页岩陶粒对混凝土破坏特征及机理影响的研究
3.
Effect of pre-wetted shale ceramsite with low water absorption on performances of high-strength lightweight aggregate concrete
低吸水率页岩陶粒预湿处理对高强轻集料混凝土性能的影响
4) shale haydite
页岩陶粒
1.
This paper shows that HPLC which 28days str ength over 30MPa and anti-permeability grade greater than P12 can be produced by that treatment shale haydite.
普通页岩陶粒吸水率偏大,对其进行表面憎水处理,可有效降低其吸水率,满足高性能轻集料混凝土(HPLC)配制的需要。
5) shale-ceramiste
页岩陶粒
1.
This text studies on the physical and chemical property of Long an county s shale-ceramiste.
对广西隆安县页岩制备的页岩陶粒进行理化性能研究。
6) shale particle
页岩陶粒
1.
This article base on producing a high performance light weight aggregate concrete with shale particle,silica fume and superplasticizer and research of the influnce of the content of cement,silice fume,and the ratio of w/c on strength,permeability and freezing resistance.
采用页岩陶粒 ,掺入硅灰和高效减水剂配制而成高性能轻集料混凝土。
补充资料：陶粒混凝土
分子式：
CAS号：
性质：又称为轻骨料混凝土(1ightaggregate concrete)。它是由胶凝材料和轻骨料配制而成的，容重不大于1900kg/m3。可分为全轻混凝土(用轻砂)与砂轻混凝土(用普通砂)。按用途可分为保温用的：密度为800kg/m3以下；结构保温用的：密度为800～1400kg/m3；结构用的：密度为1400kg/m3以上。轻骨料混凝土的耐热、防火性能较普通混凝土的好，但弹性模量则较低。以陶粒为粗骨料，以普通砂或陶砂为细骨料的轻骨料混凝土称为陶粒混凝土。结构用陶粒混凝土的强度可大于40MPa，保温及耐热性能较好。可用于房屋建筑、桥梁、船及窑炉基础等。
CAS号：
性质：又称为轻骨料混凝土(1ightaggregate concrete)。它是由胶凝材料和轻骨料配制而成的，容重不大于1900kg/m3。可分为全轻混凝土(用轻砂)与砂轻混凝土(用普通砂)。按用途可分为保温用的：密度为800kg/m3以下；结构保温用的：密度为800～1400kg/m3；结构用的：密度为1400kg/m3以上。轻骨料混凝土的耐热、防火性能较普通混凝土的好，但弹性模量则较低。以陶粒为粗骨料，以普通砂或陶砂为细骨料的轻骨料混凝土称为陶粒混凝土。结构用陶粒混凝土的强度可大于40MPa，保温及耐热性能较好。可用于房屋建筑、桥梁、船及窑炉基础等。