1) high strength pottery grain
高强度陶粒
2) high strength ceramsite
高强陶粒
1.
This paper deals with high fluid concrete in which high strength ceramsite made from shale was used as coarse aggregate.
本文采用高强页岩陶粒，掺加高效减水剂配制大流动性结构轻集料混凝土，讨论了水泥用量、水灰比、砂率、矿物掺料及轻集料的级配和预湿方式对大流动性结构轻集料混凝土强度和工作性的影响；系统研究了高强陶粒在常压和压力下的吸水规律；研究了影响大流动性结构轻集料混凝土匀质性的因素，提出了解决大流动性结构轻集料混凝土分层离析的具体措施。
4) high strength haydite castable material
高强陶粒浇注料
1.
Using grog,haydite as aggregate,high alumina cement as binder,and using compound early strength agent,the high strength haydite castable material produced successfully This castable material has the characters of early strengthened,good heat preservation,good resistance to wear,small volume density and good constraction property,etc This castable material has good utilization effect in productio
以焦宝石、陶粒为骨料 ,高铝水泥作结合剂及采用复合早强剂 ,研制成功高强陶粒浇注料。
5) high strength expanded shale
高强页岩陶粒
1.
On the basis of measurement of high strength expanded shale properties, concrete mixtures of ten different proportions with design strength of 20 MPa to 60 MPa were prepared.
在高强页岩陶粒性能测定的基础上,配制了10种不同配合比的混凝土拌和物,其设计强度为20～60MPa。
2.
A new type of asphalt mixture was prepared with high strength expanded shale and was applied successfully to pavement.
采用高强页岩陶粒制备了一种轻质、抗滑、降噪的新型沥青混合料,并将这种沥青混合料成功应用于路面工程。
6) High strength fly ash aggregate
粉煤灰高强陶粒
补充资料：高模量高强度聚合物
分子式：
CAS号：
性质： 常指杨氏模量和断裂强度分别大于100GPa和3GPa的有机聚合物。实现高强高模的途径之一是将柔性高分子进行超拉伸，使卷曲或折叠的分子链拉直，并沿拉伸方向取向成伸直链结晶；另一是合成刚性棒状液晶高分子，从根本上抑制分子链的卷曲或折叠，使分子链构象或分子链间的滑移变形大大减小，外力作用在分子链的共价键上，从而大幅度提高聚合物的强度和模量。这两种方法的代表分别有超拉伸的超高分子量聚乙烯纤维，和液晶芳香聚酰胺纤维，前者的强度和模量已达到4GPa和210GPa，后者已达到2.9GPa和110GPa。
CAS号：
性质： 常指杨氏模量和断裂强度分别大于100GPa和3GPa的有机聚合物。实现高强高模的途径之一是将柔性高分子进行超拉伸，使卷曲或折叠的分子链拉直，并沿拉伸方向取向成伸直链结晶；另一是合成刚性棒状液晶高分子，从根本上抑制分子链的卷曲或折叠，使分子链构象或分子链间的滑移变形大大减小，外力作用在分子链的共价键上，从而大幅度提高聚合物的强度和模量。这两种方法的代表分别有超拉伸的超高分子量聚乙烯纤维，和液晶芳香聚酰胺纤维，前者的强度和模量已达到4GPa和210GPa，后者已达到2.9GPa和110GPa。