1) Cordierite ultra micro powder
堇青石超微粉
2) cordierite glass-ceramics
堇青石微晶玻璃
1.
The preparation of cordierite glass-ceramics from high alumina fly ash;
利用高铝粉煤灰制备堇青石微晶玻璃的实验研究
2.
The effect of TiO_2 on microstructure and properties of cordierite glass-ceramics was discussed emphatically in this paper by using IR,XRD,SEM etc.
采用IR、XRD、SEM等现代测试方法,着重探讨了晶核剂TiO2对堇青石微晶玻璃的结构与性能的影响。
3) cordierite-based glass-ceramics
堇青石微晶玻璃
4) cordierite
[英]['kɔ:diə,rait] [美]['kɔrdɪə,raɪt]
堇青石
1.
Influence of K_2O impurity on the crystalline structure of cordierite synthesized from waste aluminum slag;
K_2O杂质对铝型材厂工业废渣合成的堇青石材料晶相结构的影响
2.
Surface modification study on cordierite honeycomb ceramics;
堇青石质蜂窝陶瓷载体的表面改性
3.
Crystallization and mechanical properties of high strength α-cordierite glass-ceramics;
高强度α-堇青石基玻璃陶瓷的析晶与力学性能
5) α-cordierite
α-堇青石
6) μ-cordierite
μ-堇青石
补充资料：堇青石陶瓷
分子式：
CAS号：
性质：堇青石(2MgO·2Al2O3·5SiO2)为主晶相的陶瓷。耐压强度280～500MPa。抗拉强度25～40MPa。抗弯强度50～60MPa。冲击强度1.8～2.2cm·kg/cm2。线膨胀系数(1.1～1.8)×10-6(20～100℃)。平均热传导率3.35～5.02kJ/(m2·h·℃)(0～100℃)。耐冷热温度300～500℃。绝缘电阻2.3～5.6MΩ·cm(400～600℃)。介质损耗角正切值200×10-4(50Hz)；40×10-4(500Hz)。耐火度约1400℃。主要原料为滑石、黏土、氧化铝、长石等。用一般陶瓷工艺制造。烧结范围较窄，烧结温度与堇青石分解温度只差几度，难获得致密体。常采用绿泥石、碳酸镁、碳酸钡、硅酸锆、二氧化锆、三氧化二硼、锂辉石等作为添加剂，能降低烧结温度，扩大烧成温度范围，并改善其介电性能。可用作线圈骨架，耐电弧作用的电绝缘材料、复合材料的基料，电热绝缘装置的燃烧器喷嘴的材料等。
CAS号：
性质：堇青石(2MgO·2Al2O3·5SiO2)为主晶相的陶瓷。耐压强度280～500MPa。抗拉强度25～40MPa。抗弯强度50～60MPa。冲击强度1.8～2.2cm·kg/cm2。线膨胀系数(1.1～1.8)×10-6(20～100℃)。平均热传导率3.35～5.02kJ/(m2·h·℃)(0～100℃)。耐冷热温度300～500℃。绝缘电阻2.3～5.6MΩ·cm(400～600℃)。介质损耗角正切值200×10-4(50Hz)；40×10-4(500Hz)。耐火度约1400℃。主要原料为滑石、黏土、氧化铝、长石等。用一般陶瓷工艺制造。烧结范围较窄，烧结温度与堇青石分解温度只差几度，难获得致密体。常采用绿泥石、碳酸镁、碳酸钡、硅酸锆、二氧化锆、三氧化二硼、锂辉石等作为添加剂，能降低烧结温度，扩大烧成温度范围，并改善其介电性能。可用作线圈骨架，耐电弧作用的电绝缘材料、复合材料的基料，电热绝缘装置的燃烧器喷嘴的材料等。