1.
Preparation of a high-strength α-hemihydrate gypsum based on complex pastern material is studied by using a complex active agent of industrial waste to improve the crystal properties of hemihydrate gypsum and to eliminate impurities' effect on the properties of products of phosphorous gypsum,such as phosphorous and fluorine.
以磷石膏为基体原料制备高强α-半水石膏基复合材料,利用工业废渣中的激发剂来改进半水石膏的结晶性质,以消除磷石膏中磷、氟等杂质对磷石膏制品性能影响,同时激发剂使具有潜在活性的矿渣得以活化,制备的低温陶瓷化磷石膏基复合材料制品兼具陶瓷和石膏性能;SEM图片表明,制备的复合材料水化后晶体结构粗大、致密。
2.
This paper presents a detailed introduction of the characteristics and status of utilization of representative industrial wastes such as fly ash, slag and steel slag, coal gangue, phosphor slag and nuclear waste etc.
详细介绍了以粉煤灰、矿渣、钢渣、煤矸石、磷渣和核废渣等为代表的固体工业废渣的物性和利用状况,并结合我国国情,论述了工业废渣综合利用的根本途径是要与建材行业清洁化发展紧密相连。
3) industrial slag
工业废渣
1.
Recovery of silver from industrial slag aggregate;
工业废渣中金属银的回收
2.
The present status of the research of glass-ceramics by industrious solid waste as materials such as industrial slag, tailings, and refining furnace slag was s ummarized.
概述了以工业废渣、尾矿尾砂、冶炼炉渣等工业固体废弃物为原料制备微晶玻璃的研究现状。
3.
, milk-white, colored (with added coloring agents) and cream (in the color of fly ash) have been successfully developed mainly using such industrial slag as porcelain scrap, glass scrap and fly ash etc.
以废瓷粉、废玻璃粉、粉煤灰等工业废渣为主要原料,添加其它常用的陶瓷原料,成功研制出乳白色、彩色(添加色料)、黄色(以粉煤灰着色)三个系列无光乳浊釉。
4) industrial waste residue
工业废渣
1.
Produce high quality cement clinker with multi-component industrial waste residue;
多组份工业废渣配料煅烧优质水泥熟料
2.
To develop few clinker high grade compound cement with utilization of industrial waste residue;
利用工业废渣研制少熟料高标号复合水泥
3.
Study of phosphorus removal composite prepared by industrial waste residue
工业废渣基除磷材料的静态吸附研究
5) industrial wastes
工业废渣
1.
Influence factors on sulfation reactions of industrial wastes in coal combustion;
工业废渣在煤燃烧中固硫的影响因素分析
2.
Test on industrial wastes used in perforated concrete brick
工业废渣混凝土多孔砖的试制
3.
Experimental research on utilization of industrial wastes to stabilize soft soil
利用工业废渣固化软土的试验研究
6) industrial residue
工业废渣
1.
Interaction of industrial residue and clinker at low W/B;
低水胶比下工业废渣与水泥熟料的相互作用
2.
The principle of alkali-activated industrial residue to prepare a kind of new two-shot grouting material was used in this paper.
根据碱激发工业废渣原理研究制备了一种新型双液注浆材料,结果表明:其凝结时间可调,初凝范围从几十秒到3h,终凝范围从30min到15h;强度高,28d强度可达30MPa;随着水灰比和粉煤灰掺量的增加,凝结时间延长,强度降低;随着水玻璃掺量的增加,强度降低,凝结时间延长;随着水玻璃模数由1增加到3。
3.
Fully and high-efficiently utilizing industrial residues t.
还论述了最大限度高效利用工业废渣来取代更多的水泥熟料是节能、节资、保护生态环境和走社会可持续发展的必由之路。
补充资料：工业炉:工业炉排烟系统
利用烟囱或机械装置将工业炉炉膛内的烟气排出炉外的系统。保证排烟通畅是工业炉正常使用的重要条件﹐排烟不通畅时﹐炉膛压力昇高﹐从炉膛四周的缝隙会逸出大量烟气而增加炉子的热损失﹐影响炉内气流的均匀分布﹐降低炉温均匀性﹐恶化操作环境。
排烟系统是由產生抽力的排烟装置和排送烟气的烟道所组成。常用的排烟装置有烟囱(图1 烟囱排烟装置 
)﹑引风机或喷射管(图2 机械排烟装置 
)等。
烟囱排烟是靠流入烟囱内热烟气密度小於烟囱外空气密度所產生的浮力﹐以克服烟道的阻力。利用引风机也可将烟气排出﹐或在排烟系统中某一部位装设一个喷射管﹐用高速喷射气体所產生的负压排出烟气。烟囱排烟不消耗动力﹐排烟温度不受限制。当排烟阻力很大而工业炉又间断运行时﹐可用引风机或喷射管排烟。喷射管适用於排除高温烟气﹔引风机适用於排除低温烟气。
烟囱分为砖砌烟囱﹑混凝土烟囱和钢板烟囱。烟道有地下烟道和架空烟道两种。地下烟道多用砖砌﹐架空烟道宜採用衬有耐火材料的钢板製成。
为了减少烟气对环境的污染﹐或因节能需要而在烟道内设置预热器时﹐都需要儘量提高烟囱高度并增加烟囱出口处的烟气流速﹐使之大於当地最大风速或至少不低於3米/秒﹐以避免烟气中的有害气体和烟尘向地面扩散。当烟囱高度达50米以上时﹐烟囱顶部的风速为地面处风速的数倍。烟气到达地面时已在离烟囱很远的地方﹐这时烟气已在逐步扩散中稀释到无害的程度。对燃烧固体燃料的工业炉﹐在排烟系统中还要设置各种形式的除尘器﹐使烟气排出时的含尘浓度降低到200微克/米3以下。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条