1) high-strength Al alloy
高强Al合金
1.
Influence of low frequency electromagnetic field on microstructures of semi-continuously cast high-strength Al alloy;
低频电磁场对半连铸高强Al合金组织结构的影响
2) high strength Al-Cu alloy 2219
高强Al-Cu合金2219
3) high strength Al-Cu alloy
高强Al-Cu合金
1.
Pulsed MIG welding process of high strength Al-Cu alloy;
高强Al-Cu合金脉冲MIG焊工艺
2.
The effects of single-wire pulsed MIG,high-speed and low-speed double-wires pulsed MIG processes on the microstructure and properties of welds of high strength Al-Cu alloy were investigated.
研究了单丝脉冲MIG焊、低速和高速双丝脉冲MIG焊对高强Al-Cu合金焊缝组织及性能的影响。
3.
The effects of the single pulse,the electromagnetic stirring and the electromagnetic stirring plus single pulse hybrid on the microstructures and properties of high strength Al-Cu alloy welds were investigated.
研究了单脉冲、电磁搅拌、电磁搅拌和单脉冲复合作用对高强Al-Cu合金MIG焊焊缝组织及性能的影响。
4) High Strength Aluminium alloy Al-Cu-Mg Alloy
高强铝合金Al-Cu-Mg合金
5) Super-high strength Al-Zn-Cu-Mg-Zr alloy
超高强Al-Zn-Cu-Mg-Zr合金
1.
Super-high strength Al-Zn-Cu-Mg-Zr alloy containing Sc was prepared by using active flux and water chilling copper mould, The ingot was homogenized, hot rolled, annealled and cold rolled into a sheet with thickness of 2.
采用活性熔剂保护熔炼,水冷铜模激冷铸造技术制备出一种含Sc超高强Al-Zn-Cu-Mg-Zr合金铸锭。
6) high Al-Zn alloy
高Al-Zn合金
1.
The plasticity and toughness of as-cast high Al-Zn alloy may be obviouslyimproved by Ti modification.
研究了Ti对高Al-Zn合金组织性能的影响,确认加Ti处理后高Al-Zn合金中异质晶核的存在,并分析测定了异质晶核的化学成分与晶体结构在此基础上提出了Ti细化高Al-Zn合金α′相的机理:异质晶核是立方体质点Al_5Ti_2Zn相,而不是一般所预料的Al_3Ti片状或块状晶
补充资料：超高强钛合金
分子式：
CAS号：
性质：室温拉伸强度超过1400MPa的钛合金。目前这类合金还处于发展阶段，如美国波音公司的研究指标为：室温拉伸强度≥1500MPa；剪切强度≥860MPa；伸长率≥8％；加载应力等于45％室温拉伸强度时的疲劳循环次数不少于10万次；断裂韧性和屈服强度的比值与4340M超高强度钢相当。比较有发展前途的是Ti8V5FelAl亚稳定β钛合金，其典型的力学性能已达到室温拉伸强度为1480MPa；伸长率为8％。
CAS号：
性质：室温拉伸强度超过1400MPa的钛合金。目前这类合金还处于发展阶段，如美国波音公司的研究指标为：室温拉伸强度≥1500MPa；剪切强度≥860MPa；伸长率≥8％；加载应力等于45％室温拉伸强度时的疲劳循环次数不少于10万次；断裂韧性和屈服强度的比值与4340M超高强度钢相当。比较有发展前途的是Ti8V5FelAl亚稳定β钛合金，其典型的力学性能已达到室温拉伸强度为1480MPa；伸长率为8％。