1) fluidity of soldering
钎料流动性
2) brazing filler metal erosion
钎料流失
3) active filler metal
活性钎料
1.
Microstructure and properties of BCu80Ni5SnTi active filler metal for brazing cubic boron nitride
钎焊立方氮化硼BCu80Ni5SnTi活性钎料的组织与性能
2.
Composition design and optimization of Cu-Ni-Sn-Ti active filler metal
Cu-Ni-Sn-Ti活性钎料成分设计与优化
3.
According to the liquidus temperature t ≥1?100℃,cold deformation total range ε ≥40%,the study designed PdNiTi and AuPdNiTi series of high temperature active filler metals,melting temperature,ability of plastic deformation.
根据液相线温度t≥ 110 0℃、冷变形总量ε总 ≥ 40 %要求设计了PdNiTi系、AuPdNiTi系列高温活性钎料 ,对 2种钎料系列的熔化特性、加工性能、润湿性进行了实验研究 。
4) active brazing filler metal
活性钎料
1.
A Hf containing Ni - base active brazing filler metal wets carbide, nitrde, oxide engineering ceramics very well.
一种含铪的镍基活性钎料对碳化物、氮化物、氧化物工程陶瓷具有满意的润湿性。
5) active brazing alloy
活性钎料
1.
Thermodynamic analysis of a Ag-Cu-Ti active brazing alloy;
Ag-Cu-Ti活性钎料热力学分析
6) activated filler metal
活性钎料
1.
The comparison analysis of the experiments show that the activated filler metal with the addition of Ti is suitable to directory brazing of Si3N4/steel, and adopting right stress relaxation layer and seal configuration will increase the joint strength obviously.
表明,含Ti活性钎料适用于Si3N4/钢的直接钎焊;合适的应力缓和层的选择以及套封结构的使用均能明显提高钎接接头强度。
补充资料：胶料挤出流动性
分子式：
CAS号：
性质： 胶料在进入挤出机加料口后，受螺杆压缩形成胶团旋转推进，在机筒与螺杆之间受剪切搅动，逐渐形成黏流体，当推进到机头时，受口裂阻挡产生静压力，并推动胶料流过口型。在进入机头后，由于受机头内壁的摩擦阻力，胶料中间部分流速变快，靠机头内壁部分流速减小，形成层流。胶料在机头内增压后流过口型，因口型直径变小流速增大，形成速度梯度，使胶料产生拉伸变形而产生膨胀状态的挤出物。
CAS号：
性质： 胶料在进入挤出机加料口后，受螺杆压缩形成胶团旋转推进，在机筒与螺杆之间受剪切搅动，逐渐形成黏流体，当推进到机头时，受口裂阻挡产生静压力，并推动胶料流过口型。在进入机头后，由于受机头内壁的摩擦阻力，胶料中间部分流速变快，靠机头内壁部分流速减小，形成层流。胶料在机头内增压后流过口型，因口型直径变小流速增大，形成速度梯度，使胶料产生拉伸变形而产生膨胀状态的挤出物。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条