1) cold material control
冷料控制
1.
Taking the TAP2000 asphalt mixture mixing equipment as an example, this paper probes concretely into the procedures of asphalt mixture production including three technological processes of the cold material control, hot material control and mixing control, and puts forward some corresponding quality control parameters.
以TAP2000型沥青混合料拌和设备为例,具体探讨了沥青混合料生产的冷料控制、热料控制、搅拌控制这3个流程,并给出了相应的质量控制参数。
2) refrigeration control
制冷控制
1.
Emerson compressor application engineering (25) Optimum refrigeration control with E2 control in modern supermarket refrigeration system (1);
美国艾默生公司压缩机应用技术讲座 第二十五讲 在现代超市制冷系统中采用E2控制器进行最优化制冷控制(一)
2.
Emerson compressor application engineering(25)——Optimum refrigeration control with E2 control in modern supermarket refrigeration system(2);
美国艾默生公司压缩机应用技术讲座 第二十五讲 在现代超市制冷系统中采用E2控制器进行最优化制冷控制(二)
3) control cooling
控制冷却
1.
The technique of control cooling is emphasized clear in principle and practice here.
概括了渗碳钢齿轮锻件等温正火处理的网带式生产线设计时主要设计参数,强调了等温正火的控制冷却技术,给出了所研制的设备的主体结构和功能的技术说明。
2.
In order to reduce production cost, the best production process using niobium microalloy instead of vanadium to produce Q345B plates of different thickness is discussed through analyzing the reason of forming Widmannstaetten structure and the influences of slab thickness, the reduction in pass, low temperature rolling and control cooling etc on the grain size and the properties.
为降低生产成本,通过分析钢板形成魏氏组织的原因以及中间坯厚度、道次变形量、低温轧制和控制冷却等对钢板组织晶粒度和性能的影响,探讨了采用铌微合金化代替钒生产不同厚度Q345B钢板的最佳生产工艺。
3.
The control cooling experiment of given-water quantity is carried out on reinforced bars Φ25 during producing.
在现场对Φ２５螺纹钢进行定水量控制冷却试验，并沿轧件全长测试了终轧温度，自回火温度和机械性能，分析了测试结果，找出了它们之间的相互关系。
4) secondary cooling control
二冷控制
1.
The improving measures include increas- ing the length of secondary cooling zones and the specific water flow,adjusting the water flow distribution among the secondary cooling zones,so the optimum secondary cooling control scheme is .
针对攀钢高强耐候乙字钢大方坯连铸二冷控制制度在连铸比水量和二冷区水量分配等方面存在的问题,通过采用延长喷水冷却区长度、适当增大连铸比水量、调整二冷区各回路的冷却能力及水量分配比例的方法,优化了YQ450NQR1大方坯连铸二冷制度。
2.
Therefore, the secondary cooling control scheme suitable for rail steel was developed on the basis of the variation of hot ductility with temperature and the distribution of strand surface temperature in secondary cooling zones, which improves internal quality of bloom heavy ra.
针对攀钢大方坯连铸引进的二冷控制技术在连铸比水量和二冷区水量分配等方面存在的问题,通过测试研究重轨钢的高温延塑性能和二冷区的铸坯表面温度分布,制定了满足攀钢重轨钢连铸工艺要求的二冷控制制度。
5) cooling control
冷却控制
1.
Melt Flow in the Extrusion Die Head for Blown Film and Application of Cooling Control Technology;
吹膜机头内熔料流动及冷却控制技术应用
2.
Dissection of the cooling control system for the shape control on an aluminium cold mill;
铝带冷轧机板形冷却控制系统剖析
3.
Application of PLC to cooling control for large transformers;
PLC在大型变压器冷却控制中的应用
6) secondary cooling scheme
二冷控制
1.
The key technologies, such as M-EMS, secondary cooling scheme, dynamic soft reduction, and its application to bloom continuous casting for heavy rail steel were presented.
简述了攀钢大方坯连铸结晶器电磁搅拌技术、二冷控制技术和凝固末端动态轻压下技术在重轨钢连铸中的应用效果。
补充资料：冷料头
分子式：
CAS号：
性质：在注塑成型中，最先进入模具内的材料，通过喷嘴和主流道时急剧冷却，此冷料进入模腔内易与其他成型材料熔接不良。此冷却了的成型材料即称冷料。冷料是造成制品质量不好的原因。为此在模具上需要开设冷料阱。
CAS号：
性质：在注塑成型中，最先进入模具内的材料，通过喷嘴和主流道时急剧冷却，此冷料进入模腔内易与其他成型材料熔接不良。此冷却了的成型材料即称冷料。冷料是造成制品质量不好的原因。为此在模具上需要开设冷料阱。