1) cool controlled rolling
控冷轧制
1.
Mathematical model of thermal process wire cool controlled rolling and its numerical simulation;
线材控冷轧制热过程数学模型及其数值仿真
2) cold tandem mill control system
冷连轧控制系统
3) controlled rolling and controlled cooling
控制轧制与控制冷却
1.
400 MPa hot-rolled ribbed bars in diameters from 6 to 10 mm were produced with plain carbon steel through controlled rolling and controlled cooling adjusting the billets' chemical composition.
采用控制轧制与控制冷却工艺,在适当调整钢坯化学成分的情况下,利用普碳钢轧制出了直径为6~10 mm的400 MPa细晶粒Ⅲ级钢筋。
4) controlled rolling / controlled cooling
控制轧制/控制冷却
5) controlled rolling and controlled cooling
控制轧制和控制冷却
1.
98, was developed by using controlled rolling and controlled cooling process.
采用C-Mn钢为原料,通过控制轧制和控制冷却工艺,试制5、6mm两种厚度规格540MPa级热轧双相钢,屈服强度365~375MPa,抗拉强度545~570MPa,断后伸长率>29%,屈强比<0。
6) control rolling and control cooling
控轧控冷
1.
Aided by the actual measurement of 1 700 mm continuous hot rolling production in WISCO,this paper studies the optimized ingredient design,control rolling and control cooling of hot-rolled strip steel T52L.
利用武汉钢铁(集团)公司热轧厂1700热连轧机大生产实测数据,对热轧带钢T52L的最佳化成分设计及控轧控冷工艺进行研究,优化T52L钢的化学成分,着重分析化学成分、轧制工艺对带钢屈服强度、抗拉强度、延伸率及冷弯性能的影响,同时进行性能控制的相关研究,建立T52L钢的力学性能控制模型,为工业化生产提供理论依据。
2.
The research on the process of control rolling and control cooling was carried out to produce the KL400Ⅲ screw bars by low carbon steel on high speed wire mill.
通过采用控轧控冷工艺，对在高线轧机上用普碳钢生产ＫＬ４００Ⅲ级螺纹钢筋进行探讨，经试轧，生产出Φ８ｍｍ的ＫＬ４００Ⅲ级螺纹钢筋。
3.
This article describes the development of hot rolled strip X52 pipeline produced by ASP in Angang, the composition design, Nb-Ti microalloying, smelting, continuous thin slab casting, control rolling and control cooling.
Ti微合金化、冶炼、连铸、薄板坯的控轧控冷等。
补充资料：可逆冷轧机电控系统
可逆冷轧机电控系统
electric drive control system for revers-ible cold-rolling mill
所示为计算机控制系统的组成示意图。它将可逆冷轧机的轧制工艺过程进行程序编制，将每道次的轧制参数艳人计算机，这些数据以数字方式存储，变换器将数字t转为棋拟盆加人控制系统，适当地方作为提供每道次数据。典型程序编制数据有轧制速度、带钢张力、厚度轧辊间隙、轧制压力极限以及卷径计算和自动减速点的计算等。 为了便于操作人员掌握工艺流程中的重要数据，在主操作台上安装了工艺数据显示装里.该装置以彩色屏幕显示，最重要的工艺数据用曲线、光带或数字显示.这些工艺数据有尺寸误差、压下位置、卷取张力、轧制速度、轧制力和卷重等。黔断┌─┐│带│├─┤│祷│└─┘┌─┐│带│├─┤│带│└─┘押”梢压下”裸作者控制压下机钩侧.计左方卷取机轧杭犷张力什飞方。取二口丫产welll\’T’，粼匀韧┌─┐ │本│ └─┘ ┌──┬─┐ │·本│月│ └──┴─┘“戒夕丽蔽阂体l||L轧机控创自动减邀最后粗过时序逻权 .出阶段操作徽招存储橄据传.开关 愉入过挂肠┌─┬───┐│本│幸 │└─┴───┘┌─────┐│橄橄转换璐│└─────┘右方X时挽控翻台计算器“‘j什但弊创，。!“霭黯橄.透钾轧侧教据.作徽妇.润 图1四辊可逆冷轧机电控系统框图静止状态下进行的，有足够的操作间歇时间，用以变换轧制方向，使主回路可以采用电枢可逆系统，也可采用 调节组成。正常卷取过程为张力调 节，冲动、穿带和断带时自动转为速 度控制。张力调节综合考虑由卷径变 化引起的速度、卷重、转动惯量、机械 损失以及加减速过程中引起动态力矩 的变化。其中关键是准确计算卷径大 小。大型可逆冷轧机均采用最大力矩 法，让电枢电流随卷径与磁通之比变 化，张力可维持不变，磁通可任意选 定，电动机可得到充分利用。在张力 控制系统中，可直接采用张力检测装 置—张力计，构成直接张力闭环控 制系统，以改进张力控制的准确性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条