1) flame retardant polyether type of polyurethane
阻燃聚醚型聚氨酯
2) polyurethane polyetherester
聚醚酯型聚氨酯
3) polyether-ester polyurethane
聚(醚-酯)型聚氨酯
1.
The polyether-ester polyurethane cellular elastomer sole was prepared using water as blowing agent.
将聚醚多元醇和聚酯多元醇的混合,以水为发泡剂,三乙烯二胺和辛酸亚锡的复合物为催化剂,1,4-丁二醇为扩链剂,聚硅氧烷为匀泡剂,可制备聚(醚-酯)型聚氨酯微孔鞋底材料,其物理机械性能优于GB10508—89指标,成本比纯聚酯型聚氨酯的低10%~15%。
4) flame retarded polyurethane materials
阻燃聚氨酯
1.
This paper introduces the current progress of flame retarded polyurethane materials containing phosphorus and halogen flame retardants .
介绍了国外含磷系、卤素系阻燃聚氨酯材料研究状况,当今研究重点主要集中在有机磷酸酯添加型阻燃剂,反应型阻燃剂以及具有阻燃特性的聚氨酯黏结剂,建议今后应将提高阻燃聚氨酯材料的综合性能和阻燃机理作为研究的重点。
5) polyetherurethane
聚醚型聚氨酯
1.
Inquing explosive polymerization in polyetherurethane adhesive synthesis;
聚醚型聚氨酯胶粘剂合成中的爆聚现象
2.
The polyetherurethane(PEU) was synthesized by one-step method for cosmetic applications by coupling poly(tetramethylene oxide)(PTMG,Mn=2000) and poly(ethylene oxide)(PEO,Mn=2000) with 4,4'-diphenylmethane diisocyanate(MDI).
聚醚型聚氨酯(PEU)用于化妆品中,由聚四亚甲基醚二醇(PTMG)和聚环氧乙烷(PEO)与4,4-二苯甲烷二异氰酸酯(MDl)采用一步法合成,结果表明PEU暴露在60℃酒精/水(80/20,体积比)溶液中放置4周后发生降解,PEU发生变质,其相对分子质量、粘度和机械性能都发生改变。
6) polyether-based polyurethane
聚醚型聚氨酯
1.
Damping properties of polyether-based polyurethanes;
聚醚型聚氨酯的阻尼性能
补充资料:聚醚型聚氨酯
分子式:
CAS号:
性质:以聚醚多元醇作为羟基组分,与二异氰酸酯或多异氰酸酯反应制成的一类聚氨酯树脂。常用的聚醚多元醇主要有二羟基聚氧化丙醚、三羟基聚氧化丙醚、二羟基聚四氢呋喃氧化丙醚等,可用于制成泡沫塑料、弹性体、胶黏剂和涂料等。制成的防腐蚀漆膜耐碱性、耐寒性、柔韧性良好。
CAS号:
性质:以聚醚多元醇作为羟基组分,与二异氰酸酯或多异氰酸酯反应制成的一类聚氨酯树脂。常用的聚醚多元醇主要有二羟基聚氧化丙醚、三羟基聚氧化丙醚、二羟基聚四氢呋喃氧化丙醚等,可用于制成泡沫塑料、弹性体、胶黏剂和涂料等。制成的防腐蚀漆膜耐碱性、耐寒性、柔韧性良好。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。