1)  low-temperature diffusion welding
低温扩散焊
2)  diffusion at low temperature
低温扩散
3)  diffusion welding with two-step temperature
双温扩散焊
1.
The systematic study on Al alloy and stainless steel joined by diffusion welding with two-step temperature is conducted by using plating Cu layer, plating Ag layer and Al-Si alloy foil as reactive materials in the case of different joining temperature and holding time.
基于铝合金与不锈钢的焊接特性,提出采用双温扩散焊新型工艺连接铝合金和不锈钢。
4)  low temprature reduction-diffusion
低温还原扩散
5)  diffusion brazing
扩散钎焊
1.
Microstructure analysis of diffusion brazing joints of Al_2O_3-TiC composite ceramic to stainless steel;
Al_2O_3-TiC复合陶瓷与不锈钢扩散钎焊接头组织分析
2.
Analysis of interfacial structure of Ti/Cu/Ti diffusion brazing heated with oxy-acetylene flame;
Ti/Cu/Ti火焰加热扩散钎焊界面组织分析
3.
The microstructure and forming mechanism of diffusion brazing interface of TiAl alloy and 42CrMo;
TiAl合金与42CrMo扩散钎焊的界面组织及形成机理
6)  diffusion bonding
扩散焊接
1.
Optimization and design of thickness of bearing steel layer diffusion bonding on titanium alloy surface;
钛合金表面扩散焊接轴承钢硬化层厚度的优化设计
2.
FEM analysis of quenching process for multi-layer diffusion bonding materials;
扩散焊接多层材料淬火过程的有限元分析
3.
Study on Diffusion Bonding Process of Metal Matrix Composites;
金属基复合材料的扩散焊接工艺研究
补充资料:焊接:扩散焊
 将焊件紧密贴合﹐在一定温度和压力下保持一段时间﹐使接触面之间的原子相互扩散形成联接的焊接方法。影响扩散焊过程和接头质量的主要因素是温度﹑压力﹑扩散时间和表面粗糙度。焊接温度越高﹐原子扩散越快。焊接温度一般为材料熔点的0.5~0.8倍。根据材料类型和对接头质量的要求﹐扩散焊可在真空﹑保护气体或溶剂下进行﹐其中以真空扩散焊应用最广。为了加速焊接过程﹑降低对焊接表面粗糙度的要求或防止接头中出现有害的组织﹐常在焊接表面间添加特定成分的中间夹层材料﹐其厚度在0.01毫米左右。扩散焊接压力较小﹐工件不產生宏观塑性变形﹐适合焊后不再加工的精密零件。扩散焊可与其他热加工工艺联合形成组合工艺﹐如热耗-扩散焊﹑粉末烧结-扩散焊和超塑性成形-扩散焊等。这些组合工艺不但能大大提高生產率﹐而且能解决单个工艺所不能解决的问题。如超音速飞机上各种鈦合金构件就是应用超塑性成形-扩散焊製成的。扩散焊的接头性能可与母材相同﹐特别适合於焊接异种金属材料﹑石墨和陶瓷等非金属材料﹑弥散强化的高温合金﹑金属基复合材料和多孔性烧结材料等。扩散焊已广泛用於反应堆燃料元件﹑蜂窝结构板﹑静电加速管﹑各种叶片﹑叶轮﹑冲模﹑过滤管和电子元件等的製造。