1) (titanium-based) oxide
钛氧化合物
2) TiO2-SiO2 composite oxide
钛硅复合氧化物
1.
The TiO2 and TiO2-SiO2 composite oxide were prepared by Sol-gel method and characterized by XRD,BET and DRS.
用溶胶-凝胶法制备了TiO2和钛硅复合氧化物,对样品进行了X射线衍射(XRD)、比表面积测试(BET)和紫外-可见漫反射光谱(DRS)分析,并以甲基橙为模拟污染物,考察了其光催化性能。
2.
Preparative methods of sol-gel,hydrolysis precipitation,hydrothermal synthesis for photocatalysts of TiO2-SiO2 composite oxide at home and abroad are introduced in this paper.
介绍了溶胶–凝胶法、水解沉淀法、水热合成法制备钛硅复合氧化物光催化剂的研究进展,评述了3种制备方法的优缺点以及添加硅对TiO2光催化活性的影响:添加硅后增大了催化剂的比表面积,提高了TiO2晶型转变温度,增强了其表面酸度,生成的Ti—O—Si键抑制了TiO2粒径的增大,拓宽了催化剂的禁带宽度,从而提高了光催化剂的催化活性。
3) titanium-aluminum bi-oxide
钛铝复合氧化物
4) composite titanium-zirconium oxides
钛锆复合氧化物
1.
Preparation and catalytic properties of composite titanium-zirconium oxides;
钛锆复合氧化物的制备及催化性能的研究
5) titanoniobium composite oxide
钛铌复合氧化物
1.
HTiNbO_5 was pre-expanded by long-chain alkylamine,then reacting with a solution containing Ti(IV) polycations,followed by calcining the obtained precursor in air,two titanoniobium composite oxides(designated as HTNO) with a high specific surface area were prepared.
HTiNbO5经用长链有机胺预支撑,再与含Ti(IV)聚合阳离子溶液反应,所得产物在空气气氛中焙烧后制备出高比表面钛铌复合氧化物。
6) titanium-silica mixed oxides
钛硅混合氧化物
1.
Three-Dimentionally Ordered macroporous titanium-silica mixed oxides were successfully synthesized by using polystyren sphere colloid crystal as the template and the sol of tetraethyl silicate and tetrabutoxy-titane as the filling fluid.
以聚苯乙烯微球离心后形成的三维规则排列的胶晶作模板,用钛酸丁酯和正硅酸乙酯分别和水、乙醇等配制成的混合溶胶填充微球之间的间隙,然后原位形成凝胶,最后通过焙烧(<5℃/min;300℃,5h;570℃,5～10h,空气流速1L/min)除去微球得到三维规则排列的大孔钛硅混合氧化物。
补充资料：钛铝金属间化合物
分子式：
CAS号：
性质：钛铝原子比为1：1的金属间化合物。为以面心立方晶格为基础的L10型有序结构。密度小，为3.91g/cm3。使用温度达1000℃。具有良好的高温比强度和比刚度。优异的抗氧化性能。可采用高温合金的制备方法制取。理想的航天航空用轻量型高温材料。
CAS号：
性质：钛铝原子比为1：1的金属间化合物。为以面心立方晶格为基础的L10型有序结构。密度小，为3.91g/cm3。使用温度达1000℃。具有良好的高温比强度和比刚度。优异的抗氧化性能。可采用高温合金的制备方法制取。理想的航天航空用轻量型高温材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条