1) radial strain energy within fracture zone
裂尖断裂区内径向应变能
2) Fracture strain energy
断裂应变能
3) fracture process zone at crack tip
裂尖断裂过程区
1.
The experimental results of pyromagnetic effect revealed in the rupture process of rheological material with defects make known that:owing to the existence of internal temperature gradient leads to the occurrence of pyromagnetic effect in the fracture process zone at crack tip.
带缺陷流变性材料破坏过程中显现出热致磁效应的实验结果表明：在材料破坏的过程中，由于内部温度梯度的存在，导致裂尖断裂过程区具有热致磁效应。
4) fracture strain
断裂应变
1.
The experiments showed that the tensile fracture strain of such PMMA specimens was nearly ten times of that un-precompressed.
实验结果表明,与未进行预压缩处理的试验片相比,预压缩处理后的试验片的拉伸断裂应变约为前者的10倍。
2.
A study is made to determine how the stress triaxiality, temperature and strain rate could influence the fracture strain of SiC particulate reinforced metal matrix composites (PRMMCs).
研究了应力三轴度、温度、应变速率对颗粒增强金属基复合材料 (PRMMCs)断裂应变的影响。
5) breaking factor strain
裂断应变
6) radial crack zone
径向裂缝区
1.
The zones near the cavity of explosion were categorized into crushing zone,radial crack zone and elastic zone based on classical failure rules.
为了进一步研究岩石中爆炸近区的变形性状,依据经典的强度破坏准则将岩石中爆炸近区分为破碎区、径向裂缝区和弹性区。
补充资料：应变能释放速率
分子式：
CAS号：
性质：在线性弹性断裂力学中，把裂纹增加单位长度所需的能量。以符号G表示。对于张开型裂纹，通常用G1表示，当G1达某一临界值G1C时，材料断裂。
CAS号：
性质：在线性弹性断裂力学中，把裂纹增加单位长度所需的能量。以符号G表示。对于张开型裂纹，通常用G1表示，当G1达某一临界值G1C时，材料断裂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条