1) aging crack
时效开裂
1.
The tendency to aging crack in Monel alloy K-500 has been investigated by means of measuringthe residual stresses.
通过残余应力的测定，研究了ＭｏｎｅｌＫ－５００合金的时效开裂。
2) crevice failure
失效开裂
3) fissuring failure
开裂失效
1.
Analysis on fissuring failure of H13 steel in warm extrusion die cavity and control measurements;
H13钢温挤压模具型腔开裂失效分析与控制
4) cracking age
开裂时间
1.
The early-age mechanical properties and drying shrinkage of high performance concrete added with fiber were studied to investigate the development of stress in restrained concrete and predict the cracking age of concrete more precisely.
为了揭示受约束混凝土内部的应力发展以及更好地预测混凝土的开裂时间,研究了纤维对高性能混凝土早龄期力学性能与干燥收缩的影响,考虑徐变、约束度等影响因素,在弹性理论基础上,推导了受约束混凝土环应力增量表达式,采用应力破坏准则预测受约束混凝土开裂时间。
5) ageing crack
时效裂变
6) ageing induced crack
时效裂纹
补充资料：穿晶开裂
分子式：
CAS号：
性质：金属材料开裂的金属学特征之一。裂纹由晶粒内部穿过。延性断裂的断口微观特征一般为韧窝状，脆性断裂的特征为解理或准解理花样。
CAS号：
性质：金属材料开裂的金属学特征之一。裂纹由晶粒内部穿过。延性断裂的断口微观特征一般为韧窝状，脆性断裂的特征为解理或准解理花样。