1) stress resistant time to crack
耐应力开裂时间
1.
The control for intrinsic viscosity ([η]) of chips and its stability([η]reduceless)are main for increasing the PET bottle stress resistant time to crack of bottle.
讨论瓶用聚酯的乙醛值、阻隔性及啤酒包装用的聚酯瓶;聚酯的结晶熔点与瓶坯注塑之间的关系,指出结晶熔点增高的原因主要是采用较高增黏工艺温度的结果;聚酯瓶耐应力开裂时间的提高对聚酯树脂来说,主要是控制切片[η]和它的稳定性([η]降小)。
2) environment stress cracking resistance
耐环境应力开裂
1.
HDPE 6360M successfully produced in a HDPE slurry plant possessed superior physical properties,good processability and high environment stress cracking resistance(ESCR).
在HDPE淤浆法工艺生产装置上,开发了具有优良的物理性能、加工性能和耐环境应力开裂(ESCR)性能的埋地排水管材专用树脂6360M。
2.
The influences of these elastomers on environment stress cracking resistance ( ESCR ) and mechanical properties of HDPE were investigated and compared with those of LLDPE .
研究了几种极性和非极性弹性体对HDPE的结晶行为、耐环境应力开裂性能及力学性能的影响,并与LLDPE的影响作了对比。
3) stress crack resistance
耐应力开裂性
4) ESCR
耐环境应力开裂
1.
Influence Factors on ESCR of PE Pipe and countermeasure;
影响聚乙烯管材耐环境应力开裂的因素及对策
2.
Factors Harmful to the ESCR of HDPE 5200B and Remedial Measures Thereof;
影响5200B树脂耐环境应力开裂性能的因素及改进措施
5) thermal stress-crack resistance
耐热致应力开裂
6) environmental stress cracking resistance
耐环境应力开裂
1.
The authors studied aging resistance,environmental stress cracking resistance(ESCR) and processability of ethylene/1-butene copolymerized medium density polyethylene speciality resin for fiber jacket,QHK15BK.
研究了乙烯/1-丁烯共聚中密度聚乙烯(MDPE)光缆护套专用料QHK15BK的耐环境应力开裂(ESCR)性能、耐老化性能和加工性能。
补充资料：环境应力开裂
分子式：
CAS号：
性质：高分子材料在受应力作用或存在较大应变时，因环境条件的影响加速开裂的现象。高分子材料的环境应力开裂与材料本身性质及环境介质性质有关。环境介质的活性是环境开裂的诱因，介质的活性降低了材料开裂时所需的能量，影响程度取决于介质和材料间的相对表面性质。此外材料内的杂质、表面划痕、加工不良等均加速环境应力开裂的产生。根据耐环境应力数据，可确定材料使用环境及合理加工条件选择的依据。
CAS号：
性质：高分子材料在受应力作用或存在较大应变时，因环境条件的影响加速开裂的现象。高分子材料的环境应力开裂与材料本身性质及环境介质性质有关。环境介质的活性是环境开裂的诱因，介质的活性降低了材料开裂时所需的能量，影响程度取决于介质和材料间的相对表面性质。此外材料内的杂质、表面划痕、加工不良等均加速环境应力开裂的产生。根据耐环境应力数据，可确定材料使用环境及合理加工条件选择的依据。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条