1) core-shell structured compounded emulsion
核壳复合乳液
1.
Testing results indicated that,nano-SiO_2 in the form of coloid and premixed with emulsifiers before dripping monomers,was favourable to the stability of core-shell structured compounded emulsion.
采用种子乳液聚合技术制备了纳米SiO_2/丙烯酸酯核壳复合乳液,研究了氧化硅形态、氧化硅加料方式、乳化剂掺量对核壳复合乳液稳定性的影响。
2) core-shell composite emulsion
核-壳复合乳液
3) core shell stype composite latexes
核-壳型复合乳液
4) core/shell composite latex
核/壳型复合乳液
5) core-shell composite latex
核壳结构复合乳液
6) core-shell emulsion polymerization
核-壳乳液聚合
1.
Several new emulsion polymerization technologies,such as core-shell emulsion polymerization,microemulsion polymerization,and latex interpenetrating polymer networks(LIPN) were i.
介绍了几种乳液聚合新技术,如核-壳乳液聚合、微乳液聚合、乳胶型互穿网络聚合(LIPN)等,并对它们在功能型含氟乳液涂层材料研究中的应用进行了展望。
2.
The fluorinated acrylate emulsion is prepared using core-shell emulsion polymerization technology.
采用核-壳乳液聚合法制备了含氟丙烯酸酯聚合物乳液,讨论了含氟单体——甲基丙烯酸六氟丁酯(HFMA)用量、复合乳化剂体系用量、引发剂用量、N-羟甲基丙烯酰胺(NMA)用量、聚合反应温度、反应时间、搅拌速度对聚合反应最终单体转化率以及乳液聚合稳定性的影响;测试了涂膜的吸水率和乳液的黏度,以考察涂膜的耐水性。
补充资料：核壳乳液聚合
分子式：
CAS号：
性质：又称种子(乳液)聚合，两阶段(或多阶段)乳液聚合，核-壳乳液聚合或复合乳液聚合。为了得到颗粒较大的聚合物，在乳液聚合中，可先加入乳液作为种子，这样在聚合过程中，单体可在加入的种子上继续聚合，而不形成新的微粒，因此可以得到颗粒较大的聚合物，这种聚合称为种子聚合。首先，通过常规的(一般为间歇式)乳液聚合或乳液共聚合制备种子胶乳，然后在种子胶乳存在下进行另一种单体或单体混合物的聚合。是新近发展起来的一种乳液聚合方法。主要用来合成各种具有不同组分以及不同形态特征的复合聚合物胶乳。
CAS号：
性质：又称种子(乳液)聚合，两阶段(或多阶段)乳液聚合，核-壳乳液聚合或复合乳液聚合。为了得到颗粒较大的聚合物，在乳液聚合中，可先加入乳液作为种子，这样在聚合过程中，单体可在加入的种子上继续聚合，而不形成新的微粒，因此可以得到颗粒较大的聚合物，这种聚合称为种子聚合。首先，通过常规的(一般为间歇式)乳液聚合或乳液共聚合制备种子胶乳，然后在种子胶乳存在下进行另一种单体或单体混合物的聚合。是新近发展起来的一种乳液聚合方法。主要用来合成各种具有不同组分以及不同形态特征的复合聚合物胶乳。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。