1) core-shell emulsion polymerization
核壳乳液聚合
1.
In order to improve water-resistant property and weather-resistant property of styrene-acylic composite emulsion,taking styrene and acrylic acid as core monomers,butyl acrylate,acrylic acid and ethylsiloxane as shell monomers,ethylsiloxane modified styrene-acylic emulsion was prepared by semi-continuous core-shell emulsion polymerization.
为提高苯丙复合乳液的耐水性和耐侯性,以苯乙烯、丙烯酸为核单体,丙烯酸丁酯、丙烯酸、乙烯基三乙氧基硅烷为壳单体,采用半连续核壳乳液聚合工艺制备苯丙复合乳液;研究了乳化剂用量、单体配比、有机硅用量等因素对乳液及涂膜性能的影响。
2.
Low temperature self-cross-linking formaldehyde-free binder for pigment printing is prepared by means of core-shell emulsion polymerization.
采用核壳乳液聚合的方法制备低温自交联的无甲醛涂料印花粘合剂。
3.
Styrene and butyl acrylate were used as raw material,and mixed emulsifier of DSB and OP-10 was used as emulsification system,and potassium persulfate was used as initiator and functional monomer-methacrylic acid was introduced to prepare styrene-acrylate latex with pre-emulsified shell monomer and core-shell emulsion polymerization method.
采用粒子设计、聚合物形态的概念,以St为核单体、BA为壳单体,十二烷基苯磺酸钠(DSB)和烷基酚聚氧乙烯醚(OP-10)的混合乳化剂为乳化体系,K2S2O(8KPS)为引发剂,引入甲基丙烯酸(MAA)功能性单体,采用壳单体预乳化的核壳乳液聚合工艺。
2) core-shell emulsion polymerization
核-壳乳液聚合
1.
Several new emulsion polymerization technologies,such as core-shell emulsion polymerization,microemulsion polymerization,and latex interpenetrating polymer networks(LIPN) were i.
介绍了几种乳液聚合新技术,如核-壳乳液聚合、微乳液聚合、乳胶型互穿网络聚合(LIPN)等,并对它们在功能型含氟乳液涂层材料研究中的应用进行了展望。
2.
The fluorinated acrylate emulsion is prepared using core-shell emulsion polymerization technology.
采用核-壳乳液聚合法制备了含氟丙烯酸酯聚合物乳液,讨论了含氟单体——甲基丙烯酸六氟丁酯(HFMA)用量、复合乳化剂体系用量、引发剂用量、N-羟甲基丙烯酰胺(NMA)用量、聚合反应温度、反应时间、搅拌速度对聚合反应最终单体转化率以及乳液聚合稳定性的影响;测试了涂膜的吸水率和乳液的黏度,以考察涂膜的耐水性。
3) core-shell emulsion polymerization
核/壳乳液聚合
1.
The methods to prepare the waterborne silicon-contained polymer,in terms of seed emulsion polymerization,core-shell emulsion polymerization,emulsifier-free emulsion polymerization,microemulsion polymerization,latex interpenetrating polymerization and et al,are discussed.
介绍了种子乳液聚合、核/壳乳液聚合、无皂乳液聚合、微乳液聚合、互穿网络聚合等制备水性含硅聚合物的方法,并对水性含硅聚合物涂料的应用做了探讨。
4) core-shell polymer emulsion
核-壳聚合物乳液
5) core/shell emulsion polymerization
核壳乳液聚合法
6) Core-Shell structure emulsion
核/壳结构聚合物乳液
补充资料：核壳乳液聚合
分子式：
CAS号：
性质：又称种子(乳液)聚合，两阶段(或多阶段)乳液聚合，核-壳乳液聚合或复合乳液聚合。为了得到颗粒较大的聚合物，在乳液聚合中，可先加入乳液作为种子，这样在聚合过程中，单体可在加入的种子上继续聚合，而不形成新的微粒，因此可以得到颗粒较大的聚合物，这种聚合称为种子聚合。首先，通过常规的(一般为间歇式)乳液聚合或乳液共聚合制备种子胶乳，然后在种子胶乳存在下进行另一种单体或单体混合物的聚合。是新近发展起来的一种乳液聚合方法。主要用来合成各种具有不同组分以及不同形态特征的复合聚合物胶乳。
CAS号：
性质：又称种子(乳液)聚合，两阶段(或多阶段)乳液聚合，核-壳乳液聚合或复合乳液聚合。为了得到颗粒较大的聚合物，在乳液聚合中，可先加入乳液作为种子，这样在聚合过程中，单体可在加入的种子上继续聚合，而不形成新的微粒，因此可以得到颗粒较大的聚合物，这种聚合称为种子聚合。首先，通过常规的(一般为间歇式)乳液聚合或乳液共聚合制备种子胶乳，然后在种子胶乳存在下进行另一种单体或单体混合物的聚合。是新近发展起来的一种乳液聚合方法。主要用来合成各种具有不同组分以及不同形态特征的复合聚合物胶乳。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条