1)  crack slab
断板分析
2)  fracture analysis
断口分析
1.
By instrumental impact test and fracture analysis, the impact property of precipitatation-hardening stainless steel FV520(B) , aged at 350,420,470,520,560,600 and 630℃ was investigated.
利用示波冲击试验和断口分析方法,对350,420,470,520,560,600,630℃时效温度处理状态下沉淀硬化不锈钢FV520(B)的冲击性能进行了比较深入的试验研究。
2.
Some in-site vibrating test and metal fracture analysis have been done to reveal that the crack of the U-shaped bolts is fatigue failure and some reference for designer is put forward.
结合桥梁—人行道系统的现场振动测试和螺栓试样断口分析结果,指出既有桥上发生的U型螺栓破断属于疲劳破坏,并提出了改进意见。
3.
On this paper, for the failure of a superheat steam pipe, via microscopic and macroscopic studies, we took the physical and chemical inspection, such as chemical composition, mechanical properties, metallographic structure, we also took the fracture analysis, then we got the failure reasons of the superheat steam pipe.
本文针对某失效过热蒸汽管道,阐述了蒸汽管道常见的失效形式,并从微观和宏观角度出发,对失效管道的化学成分、机械性能、金相组织等理化检验及断口分析方面展开研究,从而准确判断过热蒸汽管道的失效原因。
3)  Failure Analysis
断裂分析
1.
Failure Analysis of the Valve Body of the Multi-Functional Tri-Valve Set of Flow Transducer;
流量变送器多功能三阀组阀体断裂分析
4)  fracture analysis
断裂分析
1.
Fatigue and fracture analysis of defected generator rotor;
带缺陷发电机转子的疲劳断裂分析
2.
In this paper the fracture analysis on Mode I crack in orthotropic functional gradient materials is carefully studied.
本研究成果对功能梯度材料的断裂分析有重要的理论价值和工程使用价值。
3.
A special method in this paper has been presented, introduced into fracture analysis of composite plate .
但关于含裂纹各向异性材料断裂分析的保角映射方法很少见到 ,本文作者将保角映射方法推广到正交异性材料的断裂分析中去 ,并得到了系统的求解公式 ,该系列公式在复合材料断裂理论研究和工程应用中具有一定的实用价值。
5)  fracture surface analysis
断口分析
6)  fractography [fræk'tɔɡrəfi]
断口分析
1.
By means of analyses on macroscopic inspection,chemical composition,mechanical property,microstructure and fractography,the reason of cracking failure of boiler pipes is short-term overheat.
通过宏观检验、化学成分、力学性能、金相组织及断口分析 ,得出炉管爆裂主要原因是短期过热。
2.
In adition to a preiously made qualitative analysis for the fatique failure of theoutput shaft of a reducer, an estimation of the operating stresses and an estimation of theservice life of the shaft have been carried out by using the methods of fractography andfracture mechanics.
文中在减速器输出轴疲劳破坏失效定性分析的基础上,应用断口分析和断裂力学的方法,估算了引起减速器输出轴疲劳破坏的工作应力、使用寿命等。
补充资料:板成形应变分析


板成形应变分析
strain analysis of sheet metal forming

  上,即可确定其应变路径。如果只有一块坯料,应变路径可通过以不同的冲压行程增量再次冲压同一块坯料,并测量两次冲压间的应变值得到。 (邓险王先进)banehengxing yingbian fenx*板成形应变分析(strain analysis of sheetmetal forming)薄板冲压成形时对制件上应变的分布和变化的确定。薄板冲压时制件上各点的应变值很少保持一致,实际上,从一点到另一点,应变值可能有着剧烈的变化。如果某一点的成形应变达到薄板的最大允许应变量—极限变形量,就达到了薄板的成形极限。超过了这一极限,薄板就会破裂。即使制件上的绝大部分不超过成形极限,但只要有一点破裂,就应认为整个制件已破坏。如果薄板的成形极限已知,为了评估实际成形的难易并设计出能够防止制件破坏的冲压成形方案,就需要进行薄板成形应变分析。 薄板冲压成形的成功在很大程度上取决于在特定加载条件下金属的变形行为。多数可成形薄板在进行双轴向拉伸或受到拉力和压力的综合作用时,都以相似的方式变形,但是,成形应变及其分布,可能有相当的差异。这种差异是由于材料性质,如加工硬化程度,断裂应变和塑性各向异性等的不同以及材料与工艺交互影响(测量仪器影响、薄板与模具间摩擦的影响、压力机速度的影响等)而产生的。通过薄板成形应变分析可以获得冲压制件在特定变形条件下的应变分布、变形方式、高应变区域以及各种因素对成形的影响等,从而能明确经济性最佳的冲压成形条件,或防止和避免冲压制件发生破坏的途径及方法等。 在20世纪70一80年代,薄板成形应变分析已从一个试错的过程发展成为一门工程科学,成形应变和成形极限已可用应变百分比(或长度变化百分比)定量地测量,并可对两者进行比较,以确定制件的成形难度。而在此之前,一个制件是否破坏或接近破坏的程度只能通过统计生产中废品数量来确定。 薄板成形应变分析的内容主要有4部分: (l)确定冲压制件的成形应变在制件上的分布(应变分布); (2)确定制件上任一特定点的应变随制件的成形而增加的规律(冲压制件的应变历史), (3)确定薄板的成形极限,并将成形应变与之比较。成形极限通常以成形机限图表示; (4)将冲模、压力机、薄板和润滑剂当成恶化(或增加)成形应变的因素来评定。 进行薄板成形应变分析主要依靠板成形网格M.]黄技术。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。