1) Centrifugal Thermit Process
离心铝热法
2) centrifugal-thermit process
铝热-离心法
3) SHS-centrifugal process
铝热离心法
1.
The ceramic lined pipes have been produced by SHS-centrifugal process.
采用铝热离心法制备了陶瓷内衬钢管，研究了Ｎａ２Ｂ４Ｏ７ 添加剂和过铝量对陶瓷内衬致密度、组织和性能的影响。
4) aluminothermic process
铝热法
1.
Expound magnesium metallurgy with ferrosilicon process and calcium metallurgy with aluminothermic process by contracting technological conditions.
通过工艺条件对比分析,阐明了硅热法炼镁与铝热法炼钙两者工艺过程、设备条件基本相同。
5) electrical thermite method
电铝热法
6) thermite method
铝热法
1.
on recovery are discussed in chrome-boron smelting with thermite method,and the control measures are also put forward.
讨论了铝热法铬硼合金生产工艺中原料处理、渣系、热量等方面对冶炼回收率的影响,并提出了控制方法。
2.
Developing 65％～ 75％ high grade ferrotitanium with rutile as material by thermite method can achieve optimum technological requirements and good index.
采用铝热法，以金红石为原料研制 65％～ 75％的高钛铁，取得了最佳工艺技术条件和较好的指标，高钛铁含钛达 73。
3.
The main factors affecting recovering titanium with thermite method are discussed.
简述了实验室条件下用铝热法冶炼高钛铁(Ti>65%)的情况,讨论了影响钛回收率的主要素。
补充资料：离心机速率区带离心法
速率区带离心法是在离心前于离心管内先装入密度梯度介质（如蔗糖、甘油、KBr、CsCl等），待分离的样品铺在梯度液的顶部、离心管底部或梯度层中间，同梯度液一起离心。离心后在近旋转轴处（X1）的介质密度最小，离旋转轴最远处（X2）介质的密度最大，但最大介质密度必须小于样品中粒子的最小密度，即ρP＞ρm。这种方法是根据分离的粒子在梯度液中沉降速度的不同，使具有不同沉降速度的粒子处于不同的密度梯度层内分成一系列区带，达到彼此分离的目的。梯度液在离心过程中以及离心完毕后，取样时起着支持介质和稳定剂的作用，避免因机械振动而引起已分层的粒子再混合。
由于ρP＞ρm可知S＞0，因此该离心法的离心时间要严格控制，既有足够的时间使各种粒子在介质梯度中形成区带，又要控制在任一粒子达到沉淀前。如果离心时间过长，所有的样品可全部到达离心管底部；离心时间不足，样品还没有分离。由于此法是一种不完全的沉降，沉降受物质本身大小的影响较大，一般是应用在物质大小相异而密度相同的情况。常用的梯度液有Ficoll、Percoll及蔗糖。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条