1) plane trace
晶面迹线
1.
Combining ma-trix analysis of electron diffraction pattern with calculated angle between plane traces, (011)twins and also (013) twins producing local environment for Ru_7B_3 are observed in theorthorhombic M_7C_3.
—%,颗粒面积大都为1—50μm~2将电子衍射花样的矩阵分析同计算多族晶面迹线夹角的方法相结合,发现M_7C_3中不仅含有{011}孪晶,而且还含有产生Ru_7B_3局部环境特征的{013}孪晶、并建立了M_7C_3的晶体学模型。
2) crystal plane
晶面
1.
Silver gets (200) and (111) preferred orientation in stainless steel and TiN of crystal plane respectively.
银在不锈钢和TiN膜上的晶面择优取向分别为(200),(111)。
3) Crystal face
晶面
1.
In this paper,the relationship between the crystal face index and the film quality in the vapor epitaxial growth of single crystal diamond film is analyzed,and it points out that the key factor which insures the film quality is to control the experimental conditions.
分析了气相同质外延单晶金刚石膜中晶面指数与薄膜品质的关系 ,指出了控制实验条件是确保各晶面薄膜品质的关键 。
4) crystal faces
晶面
5) orientation
晶面取向
1.
Effect of Triangle Pulse Electric Current on the Orientation in Al-Si Near-eutectic Alloy;
三角波脉冲电流对近共晶Al-Si合金晶面取向的影响
2.
XRD measurement was used to study the effect of sputtering parameters on the orientation of Cr underlayers.
利用X射线衍射法对Cr底层晶面取向和磁控溅射参数之间的关系进行了研究 ,结果表明 :如果改变溅射参数 ,使沉积Cr原子获得较大的能量 ,则有利于Cr底层最终以 ( 110 )晶面择优取向。
6) interplanar spacing
晶面距
1.
The results show that the wax crystals separated from crude oil are orthorhombic crystals whose interplanar spacing is 0.
分离出的蜡结晶为正交晶型的晶体,晶面距为0。