1) PbNb_2O_6
偏铌酸铅 PbNb_2O_6
2) lead metaniobate
偏铌酸铅
1.
The system of lead metaniobate pizoelectric ceramics for high properties materials for B-ultrasonic fan scanning transducer has been studied.
研究了作为高性能B超扇扫换能器材料的偏铌酸铅压电陶瓷系统 ,实验结果表明 ,用CoO、Co2 O3及BaCO3对纯偏铌酸铅 (PbNb2 O6)进行改性 ,得到了宏观机电性能及微观结构均较好的材料。
2.
Two different kinds of sintering technology(furnace cooling and quenching) were applied to prepare lead metaniobate.
以分析纯PbO和Nb2O5为原料,采用两种不同的烧成工艺(自然冷却和快速冷却)制备了偏铌酸铅,并对其物相、孔隙率和介电性能进行了研究。
3.
In this dissertation, lead metaniobate (PbNb_2O_6 (PN)) based piezoelectric ceramic with high Curie temperature were synthesized by conventional ceramics preparation technique.
本文采用传统电子陶瓷方法制备了偏铌酸铅(PbNb_2O_6，简称PN)基高居里温度压电陶瓷，系统研究了材料的制备工艺与结构、压电性能的关系，分析了PN基陶瓷的组成、结构与压电性能之间的联系，并结合实验结果探讨了PN基陶瓷的铁电性对压电性能的影响。
3) lead metaniobate ceramics
偏铌酸铅陶瓷
4) modified lead metaniobate
改性偏铌酸铅
5) lead metaniobate piezoelectric ceramics
偏铌酸铅压电陶瓷
6) PBLN ceramics
透明偏铌酸铅钡镧陶瓷
补充资料：偏铌酸铅压电陶瓷
分子式：
CAS号：
性质：偏铌酸铅PbNb2O6为主晶相的铁电陶瓷。斜方晶系钨青铜结构。机械品质因素很低（约为11），相对介电常数低（约为20），居里温度高（570℃），并具有各向异性等特性。主要原料为四氧化三铅和五氧化二铌，加入少量添加物，采用一般电子陶瓷工艺，但冷地速率不同可形成两种晶型，如从1250℃以上快速冷却可制得铁电陶瓷，而从1250℃缓慢冷却则为反铁电相陶瓷。主要用于制作高温、高频换能器、超声探测器等。
CAS号：
性质：偏铌酸铅PbNb2O6为主晶相的铁电陶瓷。斜方晶系钨青铜结构。机械品质因素很低（约为11），相对介电常数低（约为20），居里温度高（570℃），并具有各向异性等特性。主要原料为四氧化三铅和五氧化二铌，加入少量添加物，采用一般电子陶瓷工艺，但冷地速率不同可形成两种晶型，如从1250℃以上快速冷却可制得铁电陶瓷，而从1250℃缓慢冷却则为反铁电相陶瓷。主要用于制作高温、高频换能器、超声探测器等。