1) Pb(Sc_(1/2)Nb_(1/2))O_3
钪铌酸铅
2) Pb(Fe_(1/4)Sc_(1/4)Nb_(1/2))O_3-xPbTiO_3
铌铁酸铅-铌钪酸铅
3) lead scandium tantalate
钽钪酸铅
1.
It was found that when lead titanate added into lead scandium tantalate to form lead scandium tantalate-lead titanate solid solution (1-x)Pb(Sc1/2Ta1/2)O3-xPbTiO3 (abbr.
在钽钪酸铅中加入钛酸铅,形成具有复合钙钛矿结构的钽钪酸铅 钛酸铅固溶体(1-x)Pb(Sc1/2Ta1/2)O3 xPbTiO3(简称PSTT(x)),可有效提高钽钪酸铅材料体系的居里点、降低其制备温度,从而扩大PST体系的应用范围。
2.
In this thesis, lead scandium tantalate-lead titanate (1-x) Pb(Sc1/2Ta1/2)O3-xPbTiO3 (abbr.
采用金属氧化物电子陶瓷工艺路线，制备了钽钪酸铅-钛酸铅(1-x)Pb(Sc_(1／2)Ta_(1／2))O_3-xPbTiO_3(以下简称PSTT(100x))弛豫型铁电陶瓷，使用XRD、SEM、EDAX、XPS、RAMAN等现代分析技术对PSTT(100x)弛豫型铁电陶瓷的晶相、微观形貌、组成成分、化学价态等进行了系统分析，测试和分析了PSTT(100x)铁电陶瓷的介电常数与温度、介电常数与组分、介电常数与频率、介质损耗与频率等的关系。
4) (1-x)Pb(Sc1/2Ta1/2)O3-xPbTiOa3
钽钪酸铅-钛酸铅
5) lead magnesium niobate
铌镁酸铅
1.
The complex perovskite relaxor ferroelectric ceramics, such as lead magnesium niobate (Pb(Mg_(1/3)Nb_(2/3))O_3 ,abbreviated PMN), have excellent dielectric and ferroelectric properties.
以铌镁酸铅Pb(Mg_(1/3)Nb_(2/3))O_3(简称PMN)为代表的铅基复合钙钛矿结构弛豫型铁电陶瓷,以其优良的介电、铁电性能,在多层电容器(MLCC)和高压高介电常数电容器等诸多方面,正越来越被各国学者所关注,其研究和应用都具有十分广阔的前景。
6) lead nickel niobate
铌镍酸铅
补充资料：铌镁酸铅陶瓷
分子式：
CAS号：
性质：铌镁酸铅[Pb(Mg1/2Nb2/3)O3]为主晶相的陶瓷。属于复合钙钛矿型结构的铁电陶瓷。室温下相对介电常数12600。介质损耗角正切值小于100×10-4。主要原料为四氧化三铅、碳酸镁、五氧化二铌（Nb2O5）。适当加入玻璃熔剂、三氧化二铋矿化剂和钛酸铅移峰剂，混合均匀后采用轧膜、挤膜或流延法制成薄片，涂电极后叠装，在950℃左右烧结而成。主要用于制作片式电容器之一的独石电容器。
CAS号：
性质：铌镁酸铅[Pb(Mg1/2Nb2/3)O3]为主晶相的陶瓷。属于复合钙钛矿型结构的铁电陶瓷。室温下相对介电常数12600。介质损耗角正切值小于100×10-4。主要原料为四氧化三铅、碳酸镁、五氧化二铌（Nb2O5）。适当加入玻璃熔剂、三氧化二铋矿化剂和钛酸铅移峰剂，混合均匀后采用轧膜、挤膜或流延法制成薄片，涂电极后叠装，在950℃左右烧结而成。主要用于制作片式电容器之一的独石电容器。