1) gray iron bar
灰铁型材
2) dense bars
铸铁型材
1.
In the process of dense bars horizontal continuous casting, the surface damage of dense bars is a difficult problem.
铸铁型材水平连铸过程中型材表面的拉伤问题是连铸生产过程中遇到的难题。
3) short for profile
地铁型材
4) ductile iron bars
球铁型材
1.
This machine could resolve the problem that the present horizontal continuous casting equipment could not satisfyied the extremely stable producaton of the heavy section ductile iron bars.
本文针对目前铸铁水平连铸设备由于主机设计上的不尽合理导致拉坯工艺的局限性,因而无法满足大断面球铁型材高效稳定生产的问题,以及大断面球铁型材易产生的一系列质量缺陷,开发研制出DZSL—300型大中断面铸铁水平连铸生产线,选定了合理的生产工艺,在该生产在线稳定生产出多种规格和牌号的大中断面球铁型材。
5) iron and steel material shaped
钢铁型材
6) gray cast iron composite
灰铸铁复合材料
1.
TiC particlereinforced gray cast iron composites were fabricated by an in situ reactively cast technique.
采用原位反应铸造法制备了TiC颗粒增强灰铸铁复合材料,并考察了复合材料的组织、力学性能和摩擦磨损性能。
补充资料：变断面型材挤压
变断面型材挤压
extrusion of variable cross section shapes
b ianduanmian xjngeai Jiya变断面型材挤压(extrusion of variable。rossseetion shapes)用挤压法生产断面变化的型材，有阶段变断面型材和逐渐变断面型材之分，主要用作结构材料，它们的挤压方法也有所不同。 阶段变断面型材的挤压方法有双位楔法和可拆卸模法两种: (1)双位楔法(图1)。在型材前端经第1模成形挤压后，松开压紧楔，后端部分用第2模挤压.氯篡嘟豁 图1双位楔法挤压阶段变断面型材 1一压紧楔;2一第1模;3一第2模 (2)可拆卸模法。可拆卸模由3~4个模块组成。首先将小断面的可拆卸模装在模支承中并移至桥压筒进行挤压。挤压完毕后，移开模支承，同时，将模子同型材和模支承脱开，换上可挤压大断面型材的可拆卸模，并将模支承再移至挤压筒进行挤压。 逐渐变断面型材的挤压方法有可移动模法和带锥度异形针法两种. (D可移动模法(图2)。在挤压过程中，活动模块借助于仿形尺的作用改变位置(上升或下降)，从而逐渐改变模孔的形状和尺寸，挤出逐渐变断面型材。臀 图2可移动模法挤压逐渐变断面型材 1一不动模;2一活动模块;3一保护环;4一挤压筒;5一仿形尺 (2)带锥度异形针法。采用带有锥度的异形针和相应的异形模挤压。 (王祝堂)