1) La-Ni alloy
La-Ni合金
2) Ni-La alloy
Ni-La合金
1.
The Ni-La alloy was electro-deposited in urea-NaBr melt.
在尿素-溴化钠熔体中电沉积Ni-La合金,考察了合金的沉积行为和阴极电流密度对合金组成和表面形貌的影响。
2.
Ni-La alloy coating containing La up to 22.
本研究采用适宜的络合剂，实现了从电解质水溶液中电沉积Ni－La合金，镀层中钠含量最高达22。
3) La-Mg-Ni alloy
La-Mg-Ni合金
4) La-Ni-Pt alloy
La-Ni-Pt合金
1.
Carbon nanotubes(CNTs) supported La-Ni-Pt alloy catalysts were prepared using modified polyol process with ethylene glycol,polyvinylpyrrolidone(PVP) and hydrazine as reaction medium,protective agent and reducing agent,respectively.
采用改进的多元醇还原法以乙二醇为反应介质、PVP为保护剂、水合肼为还原剂,制备了碳纳米管(CNTs)负载的La-Ni-Pt合金催化剂,并对CNTs进行了预处理。
5) Ni-La-P alloy
Ni-La-P合金
1.
The electrodeposition of Ni-La-P alloy from aqueous solutions of citric acid,phosphorous acid and ammonium chloride has been studied by linear sweep voltammetry.
为了开发含稀土的功能材料,我们研究了从水溶液中电沉积Ni-La-P合金工艺[1]。
6) Ni-P-La alloy
Ni-P-La合金
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)