The brown metallic luster La-Co and La-Co-Ni alloy powders were prepared by potentiostatic electrolysis technique in dimethylsulfoxide solution on Cu at room temperature.
La-Co合金粉末随着电解液中LaCl3和CoCl2浓度的变化,其La与Co的原子比由5:1变为1:5;La-Co-Ni合金粉末随着电解液中LaCl3浓度的增加,其La的含量由5。
2) La-Co alloy powder
La-Co合金粉末
1.
The atomic ratios of La and Co in La-Co alloy powders changed from 5:1 to 1:5 and the content of La in La-Co-Ni alloy powder was increased from 5.
La-Co合金粉末随着电解液中LaCl3和CoCl2浓度的变化,其La与Co的原子比由5:1变为1:5;La-Co-Ni合金粉末随着电解液中LaCl3浓度的增加,其La的含量由5。
3) Ni-Co alloyed powders
Ni-Co合金粉末
1.
Microstructure and mechanical properties of hot pressed compact of Ni-Co alloyed powders;
Ni-Co合金粉末的热压显微组织与力学性能研究
4) Ni-Co pre-alloyed powder
Ni-Co预合金粉末
5) Ni-Co-Fe-La-P alloy
Ni-Co-Fe-La-P合金
1.
In order to research rare earth element application in the electroless plating on the surface of glass fiber,Ni-Co-Fe-La-P alloy was prepared on the surface of glass fiber using electroless plating.
为探索稀土元素在玻璃纤维化学镀中的应用,研究了玻璃纤维表面化学镀Ni-Co-Fe-La-P合金的工艺。
6) La-Mg-Ni-Co-based alloys
La-Mg-Ni-Co系合金
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条