1) soft melting
软熔
1.
The results of laboratory test are as follows:the PCI with oxygen enriched blast can promote indirect reduction and restrain direct reduction and it can improve soft melting and reducing behavior of ore
对鞍钢2号高炉富氧喷煤球验数据的模拟计算分析表明,富氧喷煤时,高炉中,上部区域的温场无明显变化;实验室研究结果得出,富氧喷煤能促进间接还原,抑制直接还原,并能改善矿石的还原软熔行为。
2) softening-melting properties
软熔性能
1.
To improve the softening-melting properties of iron ores,some measures are suggested to take to add properly MgO in BF operation especially the new process in which the MgO-bearing pulverized coal is injected from tuyere under the condition that the MgO content in slag should be kept up.
为了改善铁矿石的高温软熔性能,重点研究了在保证炉渣中MgO含量的同时,向高炉合理添加MgO的几种方法,提出了从风口喷吹含MgO煤粉的高炉炼铁新工艺的建议。
3) cohesive zone
软熔带
1.
Numerical simulation of influence on gas flow caused by cohesive zone;
软熔带对煤气流动影响的数值模拟
2.
Development and application of the mathematical model for cohesive zone of blast furnace;
高炉软熔带数学模型的开发及应用
3.
The results show that without or with small amount of MgO in burden,the sintering productivity can be improved,and the sinters have high cold strength and narrow temperature range of cohesive zone.
研究结果表明,在烧结过程中不加或少加MgO,可提高烧结生产效率,获得冷态强度高、软熔带温度区间窄的烧结矿,从而提高高炉软熔带的透气性、降低料柱全压差。
4) soft melting system
软熔系统
1.
Automatic control of soft melting system in electrolytic tinning machine unit;
电镀锡机组软熔系统自动控制
5) soft melting point
软熔点
6) mild melt treatment
软熔处理
1.
The effects of temperature and retaining time in mild melt treatment on the bonding strength, surface morphology and porosity of tin coating are studied.
研究了软熔处理温度与保温时间对锡镀层的镀层结合力、镀层表面形貌和孔隙率的影响。
补充资料：熔盐电解法生产铌粉(见熔盐电解法生产钽粉)
熔盐电解法生产铌粉(见熔盐电解法生产钽粉)
production of niobium powder by molten salt electrolysis
rongyand+onjlefa ShengChan n.fen熔盐电解法生产妮粉(produetion。fn;obi-um powder by molten salt eleetrolysls)见熔盐电解法生产担粉。