1) crude fibre of wheat straw
麦秸粗纤维
2) Wheat straw fiber
麦秸纤维
1.
Effects of the kinds of coupling agent,amount of wheat straw fibers obtained by thermal-mechanical extraction and compatibilizer MAPP on the interfacial compatibility between wheat straw fibers and waste polypropylene as well as the mechanical properties of the composites were studied.
采用热磨提取法提取麦秸纤维,研究了硅烷偶联剂种类、麦秸纤维含量以及相容剂MAPP含量对麦秸纤维与废旧聚丙烯间的界面相容性以及制备的复合材料力学性能的影响;用扫描电镜和三维体视显微镜观察了麦秸纤维的分散性以及复合材料冲击断口形貌。
2.
The effects of the amount of KH550 coupling agent, wheat straw fiber and MAH-g-PP compatibilizer on the mechanical properties of wheat straw fiber/waste polypropylene composites were studied.
研究了偶联剂KH550、麦秸纤维以及相容剂MAH-g-PP的添加量对麦秸纤维/废旧聚丙烯复合材料力学性能的影响。
3) wheat straw cellulose
麦秸纤维素
1.
With the wheat straw cellulose as the main raw material,it was pretreated using sodium hydroxide,sulfuric acid/acetone,sodium hydroxide/hydrogen peroxide,sodium hydroxide /peroxide acetic acid,and sodium hydroxide /ethanol at room temperature,respectively.
以麦秸纤维素为主要原料,经机械法粉碎后,室温下分别采用氢氧化钠、硫酸/丙酮、氢氧化钠/过氧化氢、氢氧化钠/过氧乙酸、氢氧化钠/乙醇溶液对其进行预处理,然后按固液比1∶50加入纤维素酶液,在一定pH值、温度、时间等条件下进行酶解,通过检测酶解液中还原糖产率来评价化学法预处理麦秸纤维素的效果。
4) wheat straw fibre/polypropylene composites
麦秸纤维/PP复合材料
1.
This study aims to evaluate potentials of wheat straw fibre used as reinforcement of wheat straw fibre/polypropylene composites, and to investigate the effects of modification, fibre addition, fibre size distribution and compatilizer addition on interfacial compatibility and mechanical properties of resultant composites.
本论文以聚丙烯(PP)为基体物质、以麦秸纤维为增强材料,制造麦秸纤维/PP复合材料,探讨了热磨、改性处理、工艺条件对麦秸纤维/PP复合材料性能的影响。
6) straw fiber
秸秆纤维
1.
Study on the Effect of Straw Fiber on Properties of PBS Composite
秸秆纤维对PBS复合材料的性能影响研究
2.
The primary functional materials,including straw fiber,polyacrylamide(PAM) and super absorbent polymer(SAP),are investigated quantitatively with functional effects.
秸秆纤维、聚丙烯酰胺及高吸水树脂是基质混合物中主要的功能材料,通过试验定量研究了秸秆纤维、聚丙烯酰胺及高吸水树脂在基质混合物中的功能效应。
3.
The study on the molding technology of the straw/plastics composites and the actuality as well as the deficiency of the composites were summarized in this paper,some most potentially applicable at present were described,the characteristics and insufficiencies of straw fiber composites were analyzed.
文中从秸秆的资源状况、使用价值出发,在浅析了秸秆材料的组成结构和性能的基础上,分别介绍了秸秆纤维复合材料的成型工艺,以及复合材料制品开发应用的现状;并指出了秸秆纤维制备复合材料的优越性及复合材料制备中急需解决的问题;最后对秸秆资源综合利用及复合材料的广泛使用进行了展望。
补充资料：茶叶粗纤维检验
茶叶粗纤维检验
crude fibre inspection of tea
茶叶租纤维测定洗吸干．并重复直至洗出液呈中性为止。再将滤渣用同样浓度，数量的氢氧化钠溶液，按上法进行碱处理，直至洗下液无色为止。将残渣全部移置已知重量的无灰滤纸上过滤，再用乙醇冲洗至无色．换用乙醚冲洗若干次滤干，移至烘箱内烘至恒重，即可算出粗纤维的百分率。为厂避免泥砂物质的干扰，一般进行灰化．根据灰化后的失重量，即町算出粗纤维卣分率。此外，为了快速检测茶叶的老嫩程度，中国农业科学院茶叶研究所根据d一纤维素在茶叶纤维素中所占比例最大的特点．用17．5％氢氧化钠溶液．将茶叶煮沸20分钟后过滤，并用水清洗。直至滤液无色为止，取出烘干至恒重．即叮算出d一纤维素百分率。 (蒋德譬)茶叶粗纤维检验(erude fibre inspeetionof tea)茶叶检验之一。茶叶经稀酸、稀碱处理后对其有机残留物含量进行检测的技术措施。粗纤维主要成分是纤维素，也含少量半纤维素、木质素、角质组织、矿物质等一般茶叶中约含8~20%。随着茶叶组织老化而含量增加，与茶叶老嫩程度成正比。可作为茶叶嫩度的生化指标之一。联合国贸易和发展会议茶叶出口国会议，赞同把粗纤维检验，作为鉴别茶叶老嫩和控制低劣茶叶进入市场的手段。国际标准化组织，在“1503720一1977红茶一规格”中，已将粗纤维最高含量定为16.5%，作为红茶的标准之一。 粗纤维测定各国都用酸喊处理法。在“150 3720-1977”附录条中有规定，美国分析化学家协会(AOAC)所定的方法也基本相同。中国农业科学院茶叶研究所规定的测定方法是:取茶样5克，于烧杯中，加入1.25%的硫酸溶液200毫升.煮沸30分钟(保持200毫升容积).使酸的浓度基本不变，然后吸滤至干，加水清
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条