1) ChainExtended Diblock Polyether
双嵌段聚醚扩链产物
2) Chain Extended Diblock Polyethers
扩链双嵌段聚醚
3) oil-soluble demulsifier
双嵌段聚醚
4) block polyether
嵌段聚醚
1.
Synthesis of block polyether demulsifiers and demulsification rule;
嵌段聚醚破乳剂的合成及破乳规律
5) Block copolyether
嵌段聚醚
1.
Compared with random copolyethers,the wetting ability,emulsifying power,foam disappearing rate and solidifying temperature of block copolyethers BPE with PO block connecting to butoxyl group increase respectively by 30 times,1 time,4 times and 36 ℃,meanwhile the cloud point,surface tension,foaming ability and heat stability decrease by 32 5 ℃,8 2 mN/m,1 5 times and 55% .
与无规聚醚相比 ,PO嵌段与丁氧基相连的全嵌段聚醚BPE的润湿速度、乳化力、泡沫消失速度和凝固点分别提高 30倍、1倍、4倍和 36℃ ,浊点、表面张力、形成泡沫高度和热稳定性分别降低 32 5℃、8 2mN/m、1 5倍和 5 5 %。
2.
A EO/PO block copolyether surfactant DC218 was synthesized by the sequential addition first of propylene oxide and then ethylene oxide to propylene glycol initiator in the presence of a new type of catalyst.
以丙二醇为起始剂 ,在新型乙氧基化催化剂存在下合成出 EO/PO嵌段聚醚型表面活性剂。
6) block polyethers
嵌段聚醚
1.
We found that there are qualitative differences between block polyethers and random polyethers.
通过对聚醚的物化性质 (临界胶束浓度、乳化力、渗透性、热分解性及粘温特性 )的测试 ,得出了聚醚链段结构上环氧乙烷和环氧丙烷排列不同时对其物化性质的影响规律 ,发现嵌段聚醚和无规聚醚在其物化性质上存在“质”的区别 ,嵌段聚醚的乳化性、渗透性与热分解性质都好于无规聚醚 ,而临界胶束浓度、浊点明显低于无规聚醚 ,两者的粘温曲线相似 ,但嵌段聚醚的粘度值大于相应的无规聚
补充资料：聚碳酸酯聚二甲基硅氧烷嵌段共聚物
分子式：
CAS号：
性质：又称聚碳酸酯聚二甲基硅氧烷嵌段共聚物。分子链中同时含有聚碳酸酯和聚二甲基硅氧烷结构的嵌段共聚物。具有坚韧而透明的特点。因二甲基硅氧烷链节的引入，降低了纯聚碳酸酯(PC)的软化温度和熔融黏度，提高了冲击韧性和热分解温度范围。其薄膜的物理机械性能与PC基本相似，而氧气透过率却高约10倍。由α,ω-二氯聚二甲基硅氧烷与双酚A和光气反应制得。可用挤塑、铸塑、模塑法成型加工。主要用作宇宙飞船供氧系统、潜水艇和水下实验室呼吸系统、人工心肺机等用的薄膜。
CAS号：
性质：又称聚碳酸酯聚二甲基硅氧烷嵌段共聚物。分子链中同时含有聚碳酸酯和聚二甲基硅氧烷结构的嵌段共聚物。具有坚韧而透明的特点。因二甲基硅氧烷链节的引入，降低了纯聚碳酸酯(PC)的软化温度和熔融黏度，提高了冲击韧性和热分解温度范围。其薄膜的物理机械性能与PC基本相似，而氧气透过率却高约10倍。由α,ω-二氯聚二甲基硅氧烷与双酚A和光气反应制得。可用挤塑、铸塑、模塑法成型加工。主要用作宇宙飞船供氧系统、潜水艇和水下实验室呼吸系统、人工心肺机等用的薄膜。