1) PEEKK-PES block copolymer
聚醚醚酮酮-聚醚砜嵌段共聚物
2) PEEK-PES blends
聚醚砜-聚醚醚酮共混物
3) PEEK/PDC block copolymer
聚醚醚酮/苯酞圈型聚芳醚砜嵌段共聚物
4) poly(ether ketone ketone)/poly(ether sulfone ether ketone ketone)copolymer
聚醚酮酮/聚醚砜醚酮酮共聚物
5) polyetheretherketonesulfone
聚醚醚酮砜
1.
A series of amorphous copolymers, polyetheretherketonesulfone of high molecular weight have been prepared by bis-4 chlorophenyl sulfones, bis-4-flurophenyl ketone,the sodium salts of bis-4-hydroxyphenyl sulfone and hydroquinone as monomers in cyclobuty-sulfone.
用二氯二苯砜、二氟二苯砜、二羟基二苯酮钠盐和对苯二酚钠盐作为单体在环丁砜中制得无规共聚物系列——高分子量聚醚醚酮砜(COPEEKS)。
6) PPESK
聚醚砜酮
1.
Mechanical properties of continuous carbon fiber reinforced PPESK blends composites;
连续炭纤维增强杂萘联苯聚醚砜酮共混树脂基复合材料力学性能
2.
Preparation of PPESK based composite carbon membrane for gas separation
聚醚砜酮基炭膜的制备及其气体分离性能
3.
Nanometer and micrometer ZrO2 particle-filled poly (phthalazine ether sulfone ketone) (PPESK) composites with various filler volume fractions were prepared by heating compression molding.
采用热压成型的方法制备了纳米、微米ZrO2填充聚醚砜酮(PPESK)复合材料;考察了复合材料的显微硬度和弯曲强度;并研究了干摩擦条件下纳米、微米ZrO2颗粒对复合材料摩擦磨损性能的影响;利用扫描电子显微镜(SEM)观察分析ZrO2/PPESK复合材料磨损表面形貌及磨损机理。
补充资料：聚醚砜
聚醚砜是由4，4’-双磺酰氮二苯醚在无水氯化铁催化下，与二苯醚缩合制得。折射率1．85，玻璃化温度225℃，热变形温度203℃(1．82MPa)。耐热性介于聚砜和聚芳砜之间，长期使用温度180-200 ℃。耐老化性能优异，在180 ℃使用可达20年。耐燃性好．即使燃烧也不发烟。耐蠕变性好，在150 ℃和20MPa压力下的应变只有2．55％。耐化学药品性良好，除氯代烃、酮类、酸类以外耐一般有机溶剂。对一般酸、碱、脂肪烃、油脂、醇类等稳定。耐蒸气和过热水(150-160 ℃)性能好，耐紫外线性能较差，电性能优良，耐燃等级V-O。
相对密度 l .37-1．5l
吸水性(23℃／24h) 0. 43%
拉伸强度 84.3-124.5〔23℃)；
41．2-59．8(180℃)
伸长率 40-80％
弯曲强度 129. 4-171．5MPa
冲击强度(缺口) 78．4～85．3J／m
洛氏硬度 R120-134
相对密度 l .37-1．5l
吸水性(23℃／24h) 0. 43%
拉伸强度 84.3-124.5〔23℃)；
41．2-59．8(180℃)
伸长率 40-80％
弯曲强度 129. 4-171．5MPa
冲击强度(缺口) 78．4～85．3J／m
洛氏硬度 R120-134