1) Mesoporous ACF
中孔活性炭纤维
2) ACHF
活性中空炭纤维
1.
The adsorption capacity to iodine and methylene blue of the resultant activated hollow carbon fibers (ACHF) were tested.
聚丙烯腈(PAN)中空纤维在空气中、不同温度下预氧化2h,接着在N2气氛中炭化,CO2气氛中活化,得到PAN基活性中空炭纤维(PANACHF)。
2.
The adsorption properties of PAN-Based ACHF produced at different condition to creatinine, VB12 and bilirubin are tested.
用不同浓度的 (NH4)2HPO4溶液和不同浸渍时间处理过的聚丙烯腈 (PAN) 基中空纤维在空气中270℃预氧化,并在N2气氛下于700℃炭化,随后用CO2气体在800℃活化,测定了PAN基活性中空炭纤维对肌酐、VB12和胆红素的吸附量。
3) activated carbon hollow fiber
活性中空炭纤维
1.
Influence of carbonization process on polyacrylonitrile-based activated carbon hollow fiber;
炭化过程对聚丙烯腈基活性中空炭纤维性能的影响
2.
Effect of activation temperature on structure and adsorptivity of polyacrylonitrile-based activated carbon hollow fiber;
活化温度对聚丙烯腈基活性中空炭纤维结构和吸附性能的影响
5) mesopore activated carbon fiber
中孔活性碳纤维
1.
In recent years more uses have been found for this material with the advent of mesopore activated carbon fiber.
近年来,中孔活性碳纤维的研究拓宽了其应用领域。
6) activated carbon fiber
活性炭纤维
1.
Microwave induced activated carbon fibers catalyzed reduction for nitrogen oxide;
微波诱导活性炭纤维催化还原NO
2.
New method of electro-thermal regeneration on activated carbon fiber;
活性炭纤维电热再生新方法
3.
Adsorption of phenol from wastewater by activated carbon fiber;
活性炭纤维吸附废水中酚的研究
补充资料：聚丙烯腈基活性炭纤维
分子式：
CAS号：
性质： 由聚丙烯腈原丝制得的活性炭纤维。比表面积500～1100m2/g，直径7～16μm，平均微孔直径2～3.5nm，含氮量2％～11％，吸湿率10％～42％，苯吸附性17％～40％，乙基硫醇有效吸附性1.3％～1.8％，甲基蓝吸附性40～300ml/g。制法是将聚丙烯腈原丝经预氧化、碳化和活化而得。用途有溶剂回收、除臭和除湿剂、气液体过滤纯化材料、脱色剂、卫生材料、电子和电极材料等。
CAS号：
性质： 由聚丙烯腈原丝制得的活性炭纤维。比表面积500～1100m2/g，直径7～16μm，平均微孔直径2～3.5nm，含氮量2％～11％，吸湿率10％～42％，苯吸附性17％～40％，乙基硫醇有效吸附性1.3％～1.8％，甲基蓝吸附性40～300ml/g。制法是将聚丙烯腈原丝经预氧化、碳化和活化而得。用途有溶剂回收、除臭和除湿剂、气液体过滤纯化材料、脱色剂、卫生材料、电子和电极材料等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。