1) Fe-B compound
Fe-B化合物
2) FeB intermetallics
Fe-B金属间化合物
3) Fe-N compounds
Fe-N化合物
1.
The observation of the nitrocarburizing layer by Fractograpgy Analysis, SEM and the analysis of several process facts, the results have indicated that the reduction of the toughness of structure steel is caused by hydrogen and Fe-N compounds.
通过金相分析、扫描电子显微镜对渗层的观察及对一些工艺参数的分析,得出其主要原因是共渗过程中由于氢渗入基体,同时在晶界形成Fe-N化合物,结果导致结构钢变脆。
4) Fe-Si compounds
Fe-Si化合物
1.
The Influences of Sputtering Parameters on Formation and Structure of Fe-Si Compounds;
溅射参数对Fe-Si化合物的相形成及结构的影响
5) Fe-Sn intermetallic compound
Fe-Sn化合物
6) Fe-B alloy
Fe-B合金
1.
Using WC,Cr3C2,Fe,Co and Ni as raw materials,and adding B element with the form of Fe-B alloy and agent PVB,the slurry for green body formation was prepared.
以Fe-B合金的形式在钢结硬质合金覆层配料中添加适量的元素B和有机粘结剂PVB,球磨混合后制备成料浆,喷涂在Q235钢基体上,通过真空液相烧结技术制备钢结硬质合金覆层材料。
2.
The preparation process, structure and magnetic properties of the electroless deposition Fe-B alloy film with rare earth joined were studied.
本文研究了化学沉积稀土Fe-B合金薄膜的制备工艺、组织结构和磁学性能。
3.
The influence of cooling rate and sample purity on non-equilibrium solidification of Fe-B alloy is researched by DSC technology.
采用DSC技术研究了Fe-B合金冷却速率及试样纯度对其非平衡凝固过程的影响,得到了不同实验条件下过冷度和转变分数的演化结果,并从经典形核理论、非等温结晶动力学等方面进行了分析和讨论。
补充资料：Fe3Al基金属间化合物高温合金
Fe3Al基金属间化合物高温合金
Fe_(3)Al-base intermetallic compound superalloy
Fe3AI JIJ一nshujlon huahewu gaowen heJinFe3AI基金属间化合物高温合金(F e3AI一baseintermetallie eomPound suPeralloy)以Fe3AI相为基体的金属间化合物高温合金。该合金具有优异的高温抗氧化、抗硫化腐蚀性能，合金密度较小，因为不含贵重元素，故价格低廉，很适合于在高温氧化、硫化腐蚀的环境中工作。Fe3AI合金有两个不足之处:室温很脆，伸长率仅3%左右;高温强度不足。通过添加合金元素铬、硼，采取温加工工艺和合理的热处理制度，基本上解决了室温脆性问题，室温拉伸伸长率提高到15%左右。提高强度的途径是进行合金化，添加错、妮、铝等元素进行固溶强化和析出第二相进行时效强化，使合金室温拉伸强度达到l000MPa，600℃拉伸强度达到560MPa。Fe3AI基金属间化合物高温合金可以制造加热元件、炉子紧固件、热交换器、汽车用管材、石油管道和磁性元件等。该合金在真正走向实用之前，应在冶炼工艺和热加工工艺方面进行改进。 (}马培立卜
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条