1) intercrystalline corrosion susceptibility
晶间腐蚀敏感性
2) Sensitive erosion between crystals
晶间敏感腐蚀
4) non-sensitized intergranular corrosion
非敏化晶间腐蚀
1.
The behavior of non-sensitized intergranular corrosion (IGC) for urea grade316L stainless steel (SS) was studied by using the method of the potentiostatic etching in thetranspassive potential region and the metallograph.
采用恒电位浸蚀法配合以金相方法,研究了尿素级316L不锈钢非敏化晶间腐蚀的发展规律,比较了不同浸蚀介质、控制电位和浸蚀时间等因素的影响,结果表明:过钝化区恒电位浸蚀法可以快速、灵敏地检测奥氏体不锈钢的非敏化晶间腐蚀敏感性,使用超低磷、硅不锈钢可以减轻或消除非敏化晶间腐蚀,实验推荐下列二种检验操作条件:(1)10％草酸+0。
5) sensitized intergranular corrosion
敏化态晶间腐蚀
1.
The corrosion of X2Mod lining of urea tower was caused by the lean chromium in the heat affected zone, which was normally called the sensitized intergranular corrosion.
尿素合成塔X2Mod衬里腐蚀是由于热影响区贫铬引起的 ,即通常所说敏化态晶间腐蚀。
6) Stress Corrosion Cracking Sensitivity
应力腐蚀敏感性
1.
Influence of Different Ageing Process on Stress Corrosion Cracking Sensitivity of 2519 Aluminum Alloy Hot Rolled Plate;
时效工艺对2519铝合金热轧板材抗应力腐蚀敏感性的影响
补充资料：焊接接头晶间腐蚀
焊接接头晶间腐蚀
welded joint intercryctalline corrosion
honjle」}etou jingj旧n fush{焊接接头晶间腐蚀(welded joint intererys-talline eorrosion)在焊接接头处出现的沿晶粒边界发生的腐蚀现象。外观仍可有金属光泽，但实际上晶粒已失去联系，钢质已变脆。在奥氏体不锈钢部位有焊缝晶间腐蚀、敏化区腐蚀和刀状腐蚀等三种不同部位的晶间腐蚀。关于奥氏体不锈钢的晶间腐蚀机理有多种学说，其中以碳化物(如er23e。或(er、Fe)23e。等)在晶界沉淀现象的“贫铬理论”比较为人们所接受。所以为防止这类晶间腐蚀尽量降低含碳量，使焊缝金属含有一定量的稳定元素(如钦、妮等)以防止或降低晶界Cr23C。的形成。此外，焊缝的组织状态也有影响，单相奥氏体组织的焊缝有利于柱状晶的发达，出现贫铬层后会使腐蚀贯穿于晶粒之间，若焊缝为奥氏体了加高温铁素体占的双相组织，由于树枝状被打破，不能构成集中的腐蚀通道。高铬铁素体也会有晶间腐蚀，但与奥氏体钢不同的是从高温急冷下来即有晶间腐蚀倾向，可通过650一85oC加热、缓冷使铬扩散均匀化来消除贫铬层，防止晶间腐蚀。 (许祖泽)