Induction-refusion coating microstructure of iron-based self-fusing alloy;
感应重熔铁基自熔合金熔敷层显微组织
2.
Study on In-situ TiC Reinforced Fe-based Coating Fabricated by TIG Cladding;
钨极氩弧原位合成TiC增强铁基熔敷层的研究
3.
By using TIG welding,ferrite based composite coating reinforced with TiC has been synthesized by preplaced alloy powder which contains Ti and C on the surface of conventional carbon steel.
利用多层多道钨极氩弧熔覆技术,熔融预涂于钢基体表面钛铁和石墨混合粉末,可以在普通碳钢表面获得综合性能优异的复合材料表面熔敷层;测试和分析表明,熔敷层微观组织主要由铁素体、低碳马氏体、原位生成的TiC颗粒及碳化物等组成;熔敷层表面硬度达到了HRC 57以上,呈梯度分布特征;滑动磨损试验表明,由于TiC增强颗粒的存在,熔敷层与摩擦副的摩擦系数在磨损过程中不稳定,变化范围较大;TiC颗粒对摩擦的阻碍、钉扎作用大大提高了熔敷层的抗磨损性能,熔敷层磨损体积比基体金属小15~20倍,具有良好的耐磨性能。
2) Cu cladding layer
铜熔敷层
3) Multi-layers method
多层熔敷
4) Fe-based hardfacing layer
Fe基熔敷层
1.
,Fe-based hardfacing layer reinforced by TiC-VC particles,which were formed by the reaction among FeTi,FeV and C during welding,was produced on the substrate Q235 steel.
以H08A为焊芯,以钛铁、钒铁和石墨等为药皮组分,利用焊接电弧高温冶金反应,在Q235基体上制备TiC-VC复合超硬颗粒增强Fe基熔敷层。
5) laser cladding layer
激光熔敷层
6) laser clad layer
激光熔敷层
1.
Crack resistance and wear resistance of laser clad layer on the surface of cast iron;
铸铁表面激光熔敷层的抗裂性和耐磨性
补充资料：热熔敷
分子式：
CAS号：
性质：又称热熔敷，熔融涂布。将一些有机物，如沥青、石蜡、聚乙烯、聚丙烯、聚酰胺和聚酯等树脂类加热熔融为液体，对基材进行涂布。涂布在绝热状态下进行，用刮刀计量整饰，涂布后的纸幅经冷却器或冷缸冷却，熔融涂料在基上形成涂层，再经卷取加工成成品。特点是无环境污染，作布速度快。
CAS号：
性质：又称热熔敷，熔融涂布。将一些有机物，如沥青、石蜡、聚乙烯、聚丙烯、聚酰胺和聚酯等树脂类加热熔融为液体，对基材进行涂布。涂布在绝热状态下进行，用刮刀计量整饰，涂布后的纸幅经冷却器或冷缸冷却，熔融涂料在基上形成涂层，再经卷取加工成成品。特点是无环境污染，作布速度快。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条