1) cobaltous acetate
乙酸钴
1.
p-Nitrobenzoic acid is prepared by oxidizing p-nitrotoluene with air in acetic acid using cobaltous acetate and sodium bromide as composite catalyst.
以乙酸作溶剂，乙酸钴－ 溴化钠为复合催化剂，对硝基甲苯空气氧化制备对硝基苯甲酸。
2.
TG and DTA curve of cobaltous acetate was determined by using TG and DTA in the nitrogen and air atmosphere.
用DTA和TG测定了乙酸钴 [Co(Ac) 2 ·xH2 O]在空气和氮气中的DTA和TG曲线 运用微量X射线粉末衍射技术 ,对乙酸钴热重分解产物进行了表征 DTA、TG和XRD结果表明 ,乙酸钴有 4个结晶水 ,在空气中 ,首先失去结晶水 ,然后分解生成Co3 O4 而在氮气中 ,除失水外 ,乙酸钴分 3步分解 ,第 1步分解失去两个甲基 ,生成草酸钴 ;第 2步草酸钴进一步分解生成Co3 O4,最后生成CoO 研究乙酸钴的热分解机理将为制得高质量的锂离子电池的正负极材料提供帮
2) Bis(acetato)tetraquocobalt
乙酸亚钴
3) dithiocarbaminoacetic cobalt
氨荒乙酸钴
4) cobalt acetate tetrahydrate
乙酸钴,四水
5) Co-containing tetraethyl orthosilicate
含钴硅酸乙酯
1.
In this paper, Co-rich Co/SiO 2 composite aerogels in which mass fraction of Co can reach 66% were firstly prepared by sol-gel process of Co-containing tetraethyl orthosilicate (Co-TEOS).
本工作首次采用含钴硅酸乙酯 (Co_TEOS)进行溶胶 -凝胶反应来制备高钴含量的纳米级Co/SiO2 复合气凝胶 ,制备的Co/SiO2 复合气凝胶中n(Co)∶n(Si)的比例最高可达 2∶1,且复合气凝胶中的Co含量可在小于 6 6 % (质量分数 )的范围内任意调节 ,并系统研究了水量、催化剂浓度、溶剂量及含钴硅酸乙酯的组成对溶胶 -凝胶过程的影响 。
6) cobalt 2-ethylhexanoate
2-乙基己酸钴
补充资料：乙酸钴
分子式：C4H6CoO4·4H2O
分子量：249.09
CAS号：6147-53-1
性质：深红色单斜棱形结晶。140℃成无水物，相对密度1.705（18.7/4℃）。溶于水、酸、醇。略带醋酸气味，易潮解。
制备方法：由金属钴或氧化钴为原料，与硝酸反应制备硝酸钴溶液，再与碳酸氢铵（或纯碱）溶液反应，生成碳酸钴沉淀；将沉淀洗涤、分离，加入乙酸酸化，即可得到乙酸钴；经过滤后，将反应液调至pH=2，浓缩至溶液相对密度为1.17-1.20，然后每200L浓缩液补加1kg乙酸，在低于20℃条件下，结晶7-10d，离心分离，在30-40℃干燥即得成品。工业级乙酸亚钴含量不少于45%。原料消耗定额：金属钴（>99%）265kg/t、乙酸1000kg/t、硝酸1100kg/t。
用途：二甲苯氧化用催化剂，用于生产涂料的干燥剂、印染媒染剂、玻璃钢固化促进剂和隐显墨水等。
分子量：249.09
CAS号：6147-53-1
性质：深红色单斜棱形结晶。140℃成无水物，相对密度1.705（18.7/4℃）。溶于水、酸、醇。略带醋酸气味，易潮解。
制备方法：由金属钴或氧化钴为原料，与硝酸反应制备硝酸钴溶液，再与碳酸氢铵（或纯碱）溶液反应，生成碳酸钴沉淀；将沉淀洗涤、分离，加入乙酸酸化，即可得到乙酸钴；经过滤后，将反应液调至pH=2，浓缩至溶液相对密度为1.17-1.20，然后每200L浓缩液补加1kg乙酸，在低于20℃条件下，结晶7-10d，离心分离，在30-40℃干燥即得成品。工业级乙酸亚钴含量不少于45%。原料消耗定额：金属钴（>99%）265kg/t、乙酸1000kg/t、硝酸1100kg/t。
用途：二甲苯氧化用催化剂，用于生产涂料的干燥剂、印染媒染剂、玻璃钢固化促进剂和隐显墨水等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。