1) icrostructural evolution
枝晶衍变
1.
The microstructural evolution of A356 produced by controlled pouring during partial remelting and isothermal holding was investigated in this study.
研究了控制浇注法制备A356合金半固态枝晶衍变规律,结果表明:原始显微结构对枝晶半固态衍变具有较大影响,对于原始组织粗大的树枝晶合金,即使经过长时间的保温,初生α相仍为枝晶网状结构;而原始组织细小的等轴晶迅速转变为球状结构。
2) phase transitions
晶型衍变
1.
The relations between phase transitions and can-breaking of CTCBE and CB under different crystallization conditionswere investigated.
研究不同冷却结晶条件下CTCBE和CB的晶型衍变与胀罐的关系。
3) cell/dendrite transition
胞/枝晶转变
1.
The simulation results show that during cell/dendrite transition the mixed structure is composed of cells and dendrites,in which the secondary dendrites are absent at facing surface of some parallel closely spaced dendrites.
采用基于溶质扩散控制模型CA方法对Ti44Al合金定向凝固初始阶段变速冷却过程中胞/枝晶转变过程进行了数值模拟。
4) cellular dendritic transition
胞枝晶转变
5) cellular to dendritic transition
胞-枝晶转变
6) dendrite deformation
树枝晶变形
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。