1) alpha-silicon nitride
α-氮化硅
2) α-SiC
α-碳化硅
1.
The study onα-SiC anti-corona system modified byβ-SiC;
改进α-碳化硅防晕体系防晕性能的研究
4) β-trimethylsiloxy-α-diazo carbonyl compounds
β-三甲基硅氧基-α-重氮羰基化合物
5) silicon nitride
氮化硅
1.
Preparation of silicon nitride powder by a direct nitridation process based on fluidization technology;
基于流态化技术硅粉直接氮化制备氮化硅粉
2.
High-temperature fatigue behavior in pre-cracked silicon nitride composites doped with ytterbium oxide;
Yb_2O_3掺杂氮化硅复合材料的高温动态疲劳行为
6) Si3N4
氮化硅
1.
Machining Characters of HSWEDM Assisting Electrode Method Machining Insulated Ceramics Si3N4;
绝缘陶瓷氮化硅高速走丝线切割加工技术研究
2.
Experimental Research on ELID Precision Grinding of the Si3N4;
氮化硅材料的ELID精密磨削试验研究
3.
Si3N4 bonded SiC product was prepared by firing at 1?380?℃ for 5?h under nitrogen atmosphere with SiC,FeSi and Si powder as principal raw materials.
以碳化硅(SiC)、硅铁(FeSi)粉、硅(Si)粉为主要原料,在氮气气氛下1 380℃保温5 h制得氮化硅结合碳化硅制品,研究了硅铁粉加入量对试样常温力学性能的影响。
补充资料：氮化硅
化学式Si3N4。白色粉状晶体;熔点1900℃,密度3.44克/厘米3(20℃)；有两种变体：α型为六方密堆积结构；β型为似晶石结构。氮化硅有杂质或过量硅时呈灰色。
氮化硅与水几乎不发生作用；在浓强酸溶液中缓慢水解生成铵盐和二氧化硅；易溶于氢氟酸，与稀酸不起作用。浓强碱溶液能缓慢腐蚀氮化硅，熔融的强碱能很快使氮化硅转变为硅酸盐和氨。氮化硅在 600℃以上能使过渡金属（见过渡元素）氧化物、氧化铅、氧化锌和二氧化锡等还原,并放出氧化氮和二氧化氮。1285℃ 时氮化硅与二氮化三钙Ca3N2发生以下反应：
Ca3N2+Si3N4─→3CaSiN2
氮化硅的制法有以下几种：在1300～1400℃时将粉状硅与氮气反应；在1500℃时将纯硅与氨作用；在含少量氢气的氮气中灼烧二氧化硅和碳的混合物;将SiCl4的氨解产物Si(NH2)4完全热分解。氮化硅可用作催化剂载体、耐高温材料、涂层和磨料等。
氮化硅与水几乎不发生作用；在浓强酸溶液中缓慢水解生成铵盐和二氧化硅；易溶于氢氟酸，与稀酸不起作用。浓强碱溶液能缓慢腐蚀氮化硅，熔融的强碱能很快使氮化硅转变为硅酸盐和氨。氮化硅在 600℃以上能使过渡金属（见过渡元素）氧化物、氧化铅、氧化锌和二氧化锡等还原,并放出氧化氮和二氧化氮。1285℃ 时氮化硅与二氮化三钙Ca3N2发生以下反应：
Ca3N2+Si3N4─→3CaSiN2
氮化硅的制法有以下几种：在1300～1400℃时将粉状硅与氮气反应；在1500℃时将纯硅与氨作用；在含少量氢气的氮气中灼烧二氧化硅和碳的混合物;将SiCl4的氨解产物Si(NH2)4完全热分解。氮化硅可用作催化剂载体、耐高温材料、涂层和磨料等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。