1) Cr-graphite Fluoride Composite Coating
Cr-氟化石墨复合镀层
2) (Ni-P)-graphite composite coating
(Ni-P)石-墨复合镀层
3) Ni-Cr composite coating
Ni-Cr复合镀层
1.
The oxidation results at 750 ℃ show that the ENCCs have a superior oxidation resistance compared to EMCC, for the as-codeposited Ni-Cr composite coatings of a given Cr particles content, the finer the Cr particles, the better the .
采用复合电镀技术,通过向普通电镀溶液中分别加入平均粒度约40nm和1~5μmCr粉的方法,在Ni基材上制备了2种金属Ni基纳米Cr粒子弥散的Ni-Cr复合镀层(简称为ENCCsNi-Cr)和1种微米Cr粒子弥散的Ni-Cr复合镀层(简称为EMCCsNi-Cr)。
2.
05mol/L H2SO4 was investigated by using potentiodynamic polarization and capacitance measurement in order to investigate the effect of Cr particle sizen on the corrosion behavior of Ni-Cr composite coatings.
为了对Cr颗粒尺寸如何影响Ni-Cr复合镀层的电化学腐蚀性能有更深的认识,采用复合电镀技术,通过向普通电镀溶液中分别加入平均粒度约为40nm和1~5μm Cr粉的方法,在Ni基材上制备了2种Cr含量相近的Ni-Cr复合镀层。
4) C/Cr composite graphite-likecarbon coatings
GLC-Cr复合镀层
5) Cr/SiC composite coating
Cr/SiC复合镀层
6) C/Cr composite coating
C/Cr复合镀层
1.
The hardness,corrosion resistance,bonding force between coating and matrix and friction coefficient of the C/Cr composite coating deposited by non-equilibrium magnetron sputtering were analyzed.
采用非平衡磁控溅射在GW93镁合金表面制备了镀C/Cr复合镀层,分析了不同本底真空度下在GW93镁合金表面进行非平衡磁控溅射镀C/Cr复合镀层的硬度、耐蚀性、膜基结合力,摩擦系数等。
补充资料：氟化石墨
分子式：(CF)n
CAS号：
性质：白色粉末。从结构上看是氟进入到石墨六碳环平面层之间，与石墨相似，故称氟化石墨。热稳定性比粉末状无机高分子好。密度2.35～2.68g/cm3。没有固定熔点。分解温度在320～420℃之间，随原料种类及生成条件不同而有所变化。除浓碱、热浓硫酸外，不易被其他酸碱腐蚀。耐溶剂性、耐候性较好。表面有疏水性。有的氟化石墨氟含量小于50％，颜色显灰色或黑色且有导电性。碳氟键能很大，高温、高压以及不同气体介质中很难被切断，但仍有类似石墨的润滑性能。碳和气体氟反应制得。可用作耐高温电极、固体润滑剂等。