1) local brittle fracture stress
局部脆断应力
1.
Finite element method was employed to investigate the effects of hydrogen atoms and temper embrittlement on the local brittle fracture stress of 2.
２５Ｃｒ－１Ｍｏ钢局部脆断应力的影响。
2) local fracture stress
局部断裂应力
3) low stress brittle fracture
低应力脆断
4) local cleavage fracture stress
局部解理断裂应力
1.
Experiments were performed on different dimension and different breadth specimen of I6MnR steel , used the three point bend and four point bend load mode at ?96CC to investigate the infection of dimension breadth and load mode to local cleavage fracture stress a ~.
本文试验使用了16MnR合金钢的不同宽度和不同尺寸试样，利用了-196℃下三点弯曲和四点弯曲加载方式，进行了低温断裂实验，研究试样宽度、试样尺寸和加载方式对局部解理断裂应力σ_f的影响。
5) local stress
局部应力
1.
The local stress analysis and component design of pre-stress component anchor area;
预应力构件锚固区的局部应力分析和构造设计
2.
Experiment and submodeling analysis on local stress in main girder of prestressed concrete cable-stayed bridge;
预应力混凝土斜拉桥主梁局部应力子模型分析及试验
3.
Numerical modeling tests on local stress of SFRC tunnel segment joints;
钢纤维管片接头局部应力的数值模拟试验
6) brittle fracture stress
脆性断裂应力
补充资料：低应力脆断
分子式：
CAS号：
性质：当容器或构件采用强度高而韧性差的材料时，在应力水平不高，甚至低于材料屈服极限的情况下所发生的突然断裂现象称为低应力脆断。这类现象在使用温度较低而且选材不当时，往往发生在材料存在缺陷的地方。
CAS号：
性质：当容器或构件采用强度高而韧性差的材料时，在应力水平不高，甚至低于材料屈服极限的情况下所发生的突然断裂现象称为低应力脆断。这类现象在使用温度较低而且选材不当时，往往发生在材料存在缺陷的地方。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。