1) PPESK film
含二氮杂萘酮结构型聚醚砜酮膜
2) poly (phthalazinone ether sulfone ketone)
含二氮杂萘酮结构聚芳醚砜酮
1.
Blends of poly (phthalazinone ether sulfone ketone) (PPESK) and polytetrafluoroethylene (PTFE) were prepared via solution mixing, which was subjected to friction testing on a wear tester.
采用溶液共混法制备了不同质量比的新型含二氮杂萘酮结构聚芳醚砜酮(PPESK)与聚四氟乙烯(PTFE)共混物。
3) Poly(phthalazinone ether ketone sulfone)
含二氮杂萘结构的聚醚砜酮
4) Poly(phthalazinone ether ketone ketone)
含二氮杂萘酮结构聚芳醚酮
1.
Poly(phthalazinone ether ketone ketone) (PPEKK),a novel high heat resistant performance thermoplastic,is an amorphous PAEK.
含二氮杂萘酮结构聚芳醚酮酮 (ＰＰＥＫＫ)是一种新型耐高温聚合物 ,相比于已经商品化的各种聚芳醚酮 ,ＰＰＥＫＫ除具有优异的综合性能外 ,它最大的特点表现在以下两方面 ,ＰＰＥＫＫ耐热性突出 ,玻璃化转变温度 (Ｔｇ)为 2 4 5℃左右 ,远高于各种商品化的聚芳醚酮 ;ＰＰＥＫＫ为无定型聚合物 ,易溶于多种有机极性溶剂 ,大大的扩展了材料的应用领域且丰富了成型手段[5] 。
5) poly(phthalazinon ether sulfone) (PPES)
二氮杂萘酮聚芳醚砜(PPES)
6) sulfonated poly(phthalazinone ether ketone)
磺化二氮杂萘酮结构的聚醚酮
1.
Proton conductivity and methanol permeability of composite membranes based on sulfonated poly(phthalazinone ether ketone) doped with phosphotungstic acid;
磺化二氮杂萘酮结构的聚醚酮(SPPEK)与磷钨酸(PWA)的混合膜用两组分的DMAc混合溶液通过刮膜制备,对SPPEK/PWA膜进行了FTIR-ATR、表面形貌、质子导电性和甲醇透过性进行了研究。
补充资料：5-氨基-2,3-二氢-1,4-二氮杂萘二酮
分子式：C8H7N3O2
分子量：177.16
CAS号：521-31-3
性质：黄色结晶粉末。易溶于碱液，能溶于稀酸，几乎不溶于水，难溶于醇。中性或淡酸性溶液暴露在紫外光中时，显强烈的亮蓝色荧光。熔点329-332℃
制备方法：3-硝基苯二甲酸经环合，还原而得。将3-硝基苯二甲酸加入8%肼水溶液，加热使固体溶化。加乙二醇，在蒸发器内蒸去溶液中的过量水分，在215-220℃下加热2min，使杂环闭合，冷却后得黄色硝基化合物。冷却，加10%氢氧化钠溶液，搅拌，加入连二硫酸钠，加热至沸，保温5min，再加入乙酸，冷却得亮黄色产物。放置过夜，过滤得产物。
用途：作化学分析试剂、指示剂。
分子量：177.16
CAS号：521-31-3
性质：黄色结晶粉末。易溶于碱液，能溶于稀酸，几乎不溶于水，难溶于醇。中性或淡酸性溶液暴露在紫外光中时，显强烈的亮蓝色荧光。熔点329-332℃
制备方法：3-硝基苯二甲酸经环合，还原而得。将3-硝基苯二甲酸加入8%肼水溶液，加热使固体溶化。加乙二醇，在蒸发器内蒸去溶液中的过量水分，在215-220℃下加热2min，使杂环闭合，冷却后得黄色硝基化合物。冷却，加10%氢氧化钠溶液，搅拌，加入连二硫酸钠，加热至沸，保温5min，再加入乙酸，冷却得亮黄色产物。放置过夜，过滤得产物。
用途：作化学分析试剂、指示剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条