1) crack critical value
断裂临界值
2) hydrogen embrittlement fracture critical value
氢脆断裂临界值
3) critical rupture stress
临界断裂应力
1.
At four welding conditions of non-preheating,preheating at 100 ℃,preheating at 150 ℃ and preheating at 150 ℃ then postheating 200 ℃×2 h,the critical rupture stresses of implant test and the welding thermal cycling parameters were measured,and the fracture appearance were observed by scanning electron microscope.
通过在不预热、预热100℃、预热150℃和预热150℃并后热200℃×2 h四种焊接工艺条件下测定其插销临界断裂应力和焊接热循环参数,并对插销断口进行扫描电镜观察,综合分析了该钢的焊接冷裂纹敏感性。
2.
The influence of composition of base metal,diffusible hydrogen content,preheating temperature,plate thicknees,and strength of weld metal on the critical rupture stress within the steel are discussed.
在焊接线能量一定的条件下，定量探讨了母材成分、扩散氢含量、预热温度、板厚以及焊缝强度对临界断裂应力的影响。
4) Critical Fracture Tem perature
临界断裂温度
5) critical fracture toughness
临界断裂韧度
6) fracture critical stress
断裂临界应力
1.
With the figure of equilibrium state parameters and mathematical expressions,the tangent modulus theory which is applied to calculate the nonlinear buckling critical stress and the nonlinear fracture critical stress is recommended.
借助弹性力学中的应变能定理扩展了切线模量理论的内涵,给出了相应的平衡状态参数图及其数学表达式,并以此为基础,提出了非线性屈曲临界应力和非线性断裂临界应力计算的切线模量理论;利用切线模量理论的平衡状态模型建立了强度利用率相等模型实验原理,将其应用于疲劳试验数据的处理,提出了采用切线模量理论计算疲劳强度和断裂强度的新思路;最后对基于切线模量理论的强度稳定综合理论的发展和应用进行了展望。
补充资料：降水临界值
降水临界值
critical precipitation
1 iangshui liniiezhi降水临界值(eritieal preeipitation)在水分临界期内保证作物最小需水量的降水下限和最大需水量的降水上限值，其上、下限之间的降水量称为降水当量。降水临界值与作物的地区分布和作物类型有密切关系。如国家气象局对湖北省夫门、应城等县冬小麦降水临界期的研究，提出小麦抽穗前10一15天(水分临界期)的降水当量为30一90毫米，即在这一时段内降水量大于90毫米或小于30毫米都会使产量显著下降。而陕西省在小麦生育期内的4一5月份(水分I尚界期前后)适宜降水量的上、下限为90一110毫米。 在农业气象工作中常用降水临界最小值的概念，如北京地区壤质土，3一5月份冬小麦降水临界最小值为120一150毫米，这是保证小麦在3一5月份不受土壤干旱威胁的最少降水量。(龚绍先)