1) Critical fracture strain
临界断裂应变
2) critical rupture stress
临界断裂应力
1.
At four welding conditions of non-preheating,preheating at 100 ℃,preheating at 150 ℃ and preheating at 150 ℃ then postheating 200 ℃×2 h,the critical rupture stresses of implant test and the welding thermal cycling parameters were measured,and the fracture appearance were observed by scanning electron microscope.
通过在不预热、预热100℃、预热150℃和预热150℃并后热200℃×2 h四种焊接工艺条件下测定其插销临界断裂应力和焊接热循环参数,并对插销断口进行扫描电镜观察,综合分析了该钢的焊接冷裂纹敏感性。
2.
The influence of composition of base metal,diffusible hydrogen content,preheating temperature,plate thicknees,and strength of weld metal on the critical rupture stress within the steel are discussed.
在焊接线能量一定的条件下，定量探讨了母材成分、扩散氢含量、预热温度、板厚以及焊缝强度对临界断裂应力的影响。
3) fracture critical stress
断裂临界应力
1.
With the figure of equilibrium state parameters and mathematical expressions,the tangent modulus theory which is applied to calculate the nonlinear buckling critical stress and the nonlinear fracture critical stress is recommended.
借助弹性力学中的应变能定理扩展了切线模量理论的内涵,给出了相应的平衡状态参数图及其数学表达式,并以此为基础,提出了非线性屈曲临界应力和非线性断裂临界应力计算的切线模量理论;利用切线模量理论的平衡状态模型建立了强度利用率相等模型实验原理,将其应用于疲劳试验数据的处理,提出了采用切线模量理论计算疲劳强度和断裂强度的新思路;最后对基于切线模量理论的强度稳定综合理论的发展和应用进行了展望。
4) critical fracture stress
临界断裂应力
1.
Also,the variations of critical fracture stress at different contents of P and S with carbon content were given qualitatively.
以Ueshima的正六边形横断面枝晶模型为原型,采用有限差分方法建立了钢凝固过程伴随δ/γ相变的两相区溶质微观偏析模型,浅析了冷却速率为10℃/s的非平衡凝固条件下钢的脆性温度区内各溶质元素的偏析特点,并定量给出了不同P、S含量下脆性温度区临界断裂应力随C含量的变化规律。
5) threshold stress of environmental cracking
环境断裂临界应力
1.
The criterion of this evaluation method is:in working condition,if the threshold stress of environmental cracking of tubing and casing is no less than the percentage corresponding to the required yield strength of tubing and casing,tubing and casing would run safely.
提出了以环境断裂力学评价为基础的油套管适用性评价方法——以环境断裂临界应力百分比为基础进行管柱强度安全系数的设计。
6) crack critical value
断裂临界值
补充资料：断裂应力
分子式：
CAS号：
性质：试样破坏瞬间的应力。在材料拉伸试验中，当材料被拉断时的应力被称为拉伸断裂应力。用σb(或σy)表示，单位MPa。由于材料结构和性状的差异，由于受力状态的不同，断裂可能呈现脆性破坏和韧性破坏两种形式，断裂发生就会复杂很多，在材料力学研究中就有各种强度理论来进行描述。塑料材料对工作环境温度，加荷速率等有明显依赖关系，脆性和韧性破坏的现象会发生互相转化。
CAS号：
性质：试样破坏瞬间的应力。在材料拉伸试验中，当材料被拉断时的应力被称为拉伸断裂应力。用σb(或σy)表示，单位MPa。由于材料结构和性状的差异，由于受力状态的不同，断裂可能呈现脆性破坏和韧性破坏两种形式，断裂发生就会复杂很多，在材料力学研究中就有各种强度理论来进行描述。塑料材料对工作环境温度，加荷速率等有明显依赖关系，脆性和韧性破坏的现象会发生互相转化。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条