1) polyimide LB films
聚酰亚胺LB膜
2) LB polyimide
LB聚酰亚胺膜
3) polyimide
[英][,pɔli'imaid] [美][,pɑli'ɪm,aɪd]
聚酰亚胺膜
1.
Swelling characteristics of different polyimide membranes in ethanol-water solution;
不同结构聚酰亚胺膜在乙醇/水体系中的溶胀特性
2.
Four kinds of different structures of homogeneous polyimide (PI) membranes were prepared by two kinds of dianhydrides and two kinds of diamines.
以2种二酐、2种二胺为单体,制备了4种不同结构的聚酰亚胺(PI)均质膜;用建立的动态吸附／脱附实验装置测定水蒸气在PI膜中的吸附／脱附行为;考察了不同结构的PI膜对水蒸气吸附／脱附的影响;计算了反常扩散指数;研究了温度对水蒸气在聚酰亚胺膜(PI)中扩散系数的影响。
3.
Synthesis and Characterization of High Strength Polyimides;
机械性能测试表明BP—PI系列聚酰亚胺薄膜最大拉伸强度为960 MPa，取向纳米纤维多孔膜的拉伸强度和弹性模量分别在650MPa和15GPa动态力学性能实验结果表明：此系列聚酰亚胺膜的玻璃化转变温度在300℃以上，储能模量在18。
4) polyimide membrane
聚酰亚胺膜
1.
Effect of gelation medium on gelation rate and cross-sectional morphology of polyimide membrane
凝胶介质对聚酰亚胺膜凝胶速率及膜断面结构的影响
2.
The equilibrium solubility of alcohol and water in two polyimide membranes measured in a previous work is correlated by the dual - mode theory with Flory-Huggins solution model and Langmuir adsorption model.
用Flory-Huggins溶液模型加Langmuir吸附模型的双重模式理论关联了前文测得的乙醇和水在聚酰亚胺膜中的平衡溶解度,根据吸收/解吸数据求取了扩散系数,溶解度系数及渗透率;用无限稀释理想分离因子评价渗透蒸发膜的分离性能。
3.
The polyimide membrane was synthesized by the two-step method and its pervaporation performance for the octane and thiophene mixture was characterized.
0%的聚酰亚胺膜在膜室的温度为50℃条件下进行渗透蒸发实验,膜的渗透通量为1。
6) polyimide film
聚酰亚胺胺薄膜
补充资料：聚酰亚胺
| 聚酰亚胺 polyimides 主链含重复的酰亚胺基团  的聚合物 。英文缩写PI。结构为 式中Ar1和Ar2代表不同的芳环 。聚酰亚胺是综合性能最佳的有机高分子材料之一，耐高温达 400℃以上 ，长期使用温度范围－200～300℃，无明显熔点，高绝缘性能，103 赫下介电常数4.0，介电损耗仅0.004～0.007，属F至H级绝缘材料，耐高辐射，耐腐蚀，耐火焰，不吸水，高机械强度。其纤维的拉伸模量达0.882牛顿／旦，模压制品的模量29.4×104牛顿／厘米2，强度7252牛顿／厘米2。 此外还有较强的粘合能力。聚酰亚胺常采用溶液缩聚 ，溶剂为强极性的二甲基乙酰胺、二甲基甲酰胺、二甲基亚砜等。二酐与二胺在溶液中先缩合成高分子量的聚酰胺酸，然后逐步加热脱水固化，也可在常温下化学脱水固化。应用最广泛的是由均苯四酸酐和4，4’-二氨基二苯醚合成的聚酰亚胺，国际商品名Kapton。 聚酰亚胺可浸渍或流延成膜 ，也可干纺或湿纺成纤维，或直接涂覆成型。在航空、航海、空间、原子能、电子工业中广泛应用，也可作耐高温胶粘剂和涂料。聚酰亚胺的加工性能欠佳，可通过共聚改进，但同时会影响它的耐热性和高温机械性能。 |