1) slags of porcelain stone
瓷石尾砂
1.
Succeessfully using slags of porcelain stone as the main raw material on the basis of the proper batch formula and man-ufacturing melting method process.
根据瓷石尾砂的矿物工艺特性，采用合理科学的配方和相应的熔融法生产工艺技术，以瓷石尾砂为主要原料，取代石英砂和部分熔剂原料，成功地研制出尾砂玻璃马赛克，产品性能按国标GB7697-87检测，各项指标完全达到要求。
2.
A one time low temperature fast firing external tile is developed by using slags of porcelain stone and phyuite as main raw materials and red - clay and reducing firing temperature materials as well, prepared under low temperatureand fast firing schedule.
以瓷石尾砂和千枚岩为主要原料，外加红粘土及助熔剂原料，研制出一次低温快烧的外墙砖，烧成温度1110℃，周期60分钟，性能达到国标要求。
2) porcelain sandstone
瓷砂石
4) quartz tailing
石英尾砂
1.
Laboratory test and pilot test on production of cement with quartz tailing and waste citric acid gypsum;
利用石英尾砂和柠檬酸废渣石膏生产水泥的研究及实践
5) fluorite slag
萤石尾砂
1.
The preparation of water permeable ceramic brick using fluorite slag and perlite waste powders
利用萤石尾砂和珍珠岩废矿粉研制陶瓷透水砖
6) tailing dinax
尾矿砂石
1.
Experimental research on the construction performance of the tailing dinax concrete
尾矿砂石混凝土施工性能的试验研究
补充资料：瓷石
分子式：
CAS号：
性质：制作瓷器的一种石质原料。其矿物组成主要为石英、长石、绢云母和高岭石等，含少量蒙脱石或多水高岭石，尚有玉髓、白云石、褐铁矿等。主要化学成分为：SiO2(一般>70%)，A12O3(一般<20%)，少量K2O，Na2O，Fe2O3(一般<1%)，CaO及MgO等。呈灰白，青灰色。斑状或残余斑状结构、致密块状或疏松土块状结构。可塑性低，干燥强度高，收缩率大，煅烧后呈白色。主要用于生产瓷器、面砖瓷。
CAS号：
性质：制作瓷器的一种石质原料。其矿物组成主要为石英、长石、绢云母和高岭石等，含少量蒙脱石或多水高岭石，尚有玉髓、白云石、褐铁矿等。主要化学成分为：SiO2(一般>70%)，A12O3(一般<20%)，少量K2O，Na2O，Fe2O3(一般<1%)，CaO及MgO等。呈灰白，青灰色。斑状或残余斑状结构、致密块状或疏松土块状结构。可塑性低，干燥强度高，收缩率大，煅烧后呈白色。主要用于生产瓷器、面砖瓷。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条