1) medium high carbon alloy
中高碳合金
2) high carbon medium-alloy steel
高碳中合金钢
1.
Transformation and morphology of carbides in high carbon medium-alloy steels during transforming process;
三种高碳中合金钢在热处理过程中的碳化物转变及形貌
2.
The investigation shows that M23C6 and M3C in Cr-W-Mo-V high carbon medium-alloy steels gradually dissolve into the matrix during heat process at about αγ temperature, and gradually precipitate again from the matrix during low cooling process.
研究表明,Cr-W-Mo-V高碳中合金钢加热至αγ温度区附近,M23C6和M3C会逐渐溶解于基体中,缓冷过程逐渐析出M23C6、M3C,并在αγ温度区发生M23C6M6C转变,而球状VC则变化不大,其碳化物超细化主要南溶解、形核的转变过程所引起的。
3) high-carbon medium-chromium alloy steel
高碳中铬合金钢
1.
The high-carbon medium-chromium alloy steel was austemper heat treated, and the optimum chemical composition was determined using orthogonal design.
1%C、3%~5%Cr的高碳中铬合金钢进行了等温淬火热处理,采用正交设计确定最佳化学成分配比,得到理想配合的材料韧性和硬度,将所得高碳钢与低碳钢复合铸造双金属复合衬板。
4) MCHAHS
中碳高合金高强度钢
1.
In this paper,through analysis of austenite-ferrite transformation in MCHAHS, taking the change of lattice parameters in phases into account,a ne.
以中碳高合金高强度钢(MCHAHS)的奥氏体-铁素体相变过程为主要研究对象,通过确定冷却过程中各生成相的晶格常数随温度的变化关系,发展了一种新的由线膨胀量信息提取相变动力学信息的计算方法。
6) high boron middle-carbon wear-resistant alloy
高硼中碳耐磨合金
补充资料：高硼低碳高温合金
分子式：
CAS号：
性质：一种镍基铸造高温合金。硼含量为0.05％～0.2％，碳含量小于0.05％，不同于普通铸造镍基合金的硼为0.005％～0.03％和碳为0.1％～0.25％。高硼低碳高温合金在保持普通镍基铸造高温合金高温强度的同时，中温性能特别是塑性显著提高，如Mar-M200合金在980℃时具有很高的持久强度、蠕变强度和良好的塑性，但760℃的持久塑性几乎为零，而其改型的高硼低碳B-1950合金在保持Mar-M200合金980℃优越性能的同时，760℃的持久塑性可达2％～5％。主要用于制做发动机涡轮叶片和整体铸造涡轮转子。
CAS号：
性质：一种镍基铸造高温合金。硼含量为0.05％～0.2％，碳含量小于0.05％，不同于普通铸造镍基合金的硼为0.005％～0.03％和碳为0.1％～0.25％。高硼低碳高温合金在保持普通镍基铸造高温合金高温强度的同时，中温性能特别是塑性显著提高，如Mar-M200合金在980℃时具有很高的持久强度、蠕变强度和良好的塑性，但760℃的持久塑性几乎为零，而其改型的高硼低碳B-1950合金在保持Mar-M200合金980℃优越性能的同时，760℃的持久塑性可达2％～5％。主要用于制做发动机涡轮叶片和整体铸造涡轮转子。