1) NH_3TPD
程序升温氨脱附
1.
he effects of preparation conditions on the acidic property of SO_4~(2-)/ZrO_2 superacid catalysts have been studied by NH_3TPD technique.
用程序升温氨脱附研究了Ｈ２ＳＯ４的浓度、焙烧温度、氨水的浓度和锆前体的晶型等制备参数对ＳＯ４２－／ＺｒＯ２催化剂的酸性质的影响。
2) temperature-programmed desorption of ammonia
氨程序升温脱附
3) temperature-programmed desorption
程序升温脱附
1.
Study on adsorption of NO_x over CoH-FBZ by temperature-programmed desorption technique;
程序升温脱附研究CoH-FBZ上NO_x的吸附
2.
The results of nitrogen adsorption and temperature-programmed desorption show that the carbon supports have almost identical porous texture but different types and amounts of surface oxyge.
对炭载体的氮吸附和程序升温脱附的表征结果表明,活性炭经过硝酸氧化处理和氢气高温处理后,活性炭的孔结构基本不变,但表面含氧官能团的数量和种类发生了变化。
3.
Ni/γ-Al2O3 catalysts prepared by three different ways,general reduction(GR),plasma reduction after calcination(PR),and plasma direct reduction without calcination(PDR),were investigated by temperature-programmed desorption(TPD) with H2 and CO2,X-ray diffraction,and N2 adsorption.
用程序升温脱附(TPD)手段考察了常规焙烧还原(GR)、焙烧后等离子体还原(PR)、未焙烧等离子体直接还原(PDR)三种方法制备的Ni/-γAl2O3催化剂的H2和CO2的吸附-脱附性能,并用X射线衍射和N2吸附方法进行了表征。
4) TPD
程序升温脱附
1.
Based on determination of the kinetic model equation of TPD,a new simulation method used to characterize the surface acid strength was developed by using one group of TPD experimental data.
通过推导脱附动力学方程及确定脱附活化能参数的估值方法,建立了基于单套程序升温脱附(TPD)数据确定固体酸催化剂脱附活化能的动力学模拟方法。
2.
Static adsorption,dynamic adsorption,TPD and TPR were used to investigate the adsorption and desorption of thiophene on the nickel based amorphous alloy.
应用静态吸附、动态吸附、程序升温脱附和程序升温还原等实验方法,考察了噻吩在Ni基非晶态合金上的吸附和脱附行为。
3.
A temperature-programmed desorption (TPD) kinetic model related with heating rate, temperature and n-Propylamine overlay fraction of catalyst surface acid sites at maximum rate of desorption was determined, and a method characterizing acid density, acid strength and the distribution extent of acid strength was developed.
在确定关联升温速率、脱附峰温和脱附峰覆盖率的程序升温脱附动力学模型的基础上,通过TPD实验和模型参数估值,建立了表征催化剂酸密度、酸强度及强度分布情况的方法。
5) CO-TPD
CO程序升温脱附
6) TPD
程序升温脱附(TPD)
补充资料：程序升温脱附
分子式：
CAS号：
性质：TPD将已吸附了吸附质的吸附剂或催化剂按预定的升温程序(如等速升温)加热，得到吸附质的脱附量与温度关系图的方法。主要用于考察吸附质与吸附剂或催化剂之间的结合情况，可获得催化剂表面性质，活性中心，表面反应等方面的信息。例如用NH3TPD测量表面酸性，CO2 TPD测量表面碱性等。脱附谱包含的信息有峰的数目(与结合状态数有关)，峰极大处的温度值和各种结合状态的分子数(正比于每个峰的面积)。对图谱随加热速度和初始覆盖度变化的分析，可得出每一结合状态的其他信息，如脱附活化能，脱附速率常数的指前因子和脱附动力学级数。
CAS号：
性质：TPD将已吸附了吸附质的吸附剂或催化剂按预定的升温程序(如等速升温)加热，得到吸附质的脱附量与温度关系图的方法。主要用于考察吸附质与吸附剂或催化剂之间的结合情况，可获得催化剂表面性质，活性中心，表面反应等方面的信息。例如用NH3TPD测量表面酸性，CO2 TPD测量表面碱性等。脱附谱包含的信息有峰的数目(与结合状态数有关)，峰极大处的温度值和各种结合状态的分子数(正比于每个峰的面积)。对图谱随加热速度和初始覆盖度变化的分析，可得出每一结合状态的其他信息，如脱附活化能，脱附速率常数的指前因子和脱附动力学级数。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。