1) metallized agglomerate
金属化团块
1.
Aimed at utilization of iron resources in pyritic slag,the study on production of metallized agglomerate with pyritic slag through coal based DR process was conducted.
为合理利用硫酸烧渣中的铁资源，进行了煤基直接还原生产金属化团块的研究，提出了润磨造球-预热焙烧-磁选-冷固结成型的新工艺流程。
2) Metallized pellet
金属化球团
1.
As content ironore concentrates, not only high-quality metallized pellets, as electric furnace charge, wereobtained.
针对含锡锌砷超标的铁精矿采用球团直接还原工艺，既获得了供电炉炼钢用的优质金属化球团，又有效地脱除了产品中锻锌砷等杂质，脱除率达到90％以上。
3) metallic pellet
金属化球团
1.
The study on the bond mechanism of metallic pellet produced from Zn-Pb-bearing iron and steel plant dust with carbon shows that its compression strength is not only dependent on the shape and amount of iron phase but also on the size of hole in metallic pellet.
对含锌铅钢铁厂粉尘配碳球团，经还原焙烧后得到的高炉用金属化球团的固结机理进行了研究。
4) catalysis/metallizing pellet
催化/金属化球团
5) metal cluster compound
金属团簇化合物
1.
Study on the optical limiting properties of the new metal cluster compound;
新型金属团簇化合物的光限幅特性研究
2.
The nonlinear optical effect of metal cluster compound W2Ag4S8(dppf)2 was investigated using frequency-doubled, Q-switched Nd-YAG pulse laser system with wavelength of 532 nm and pulse width of 8 ns.
用Z扫描方法测量了金属团簇化合物W2Ag4S8(dppf)2的非线性光学响应,发现团簇W2Ag4S8(dppf)2具有显著的反饱和吸收和自聚焦等非线性光学性质。
3.
The optical limiting properties of the new metal cluster compound W\-2Cu\-4S\-6O\-2(C\-\{34\}H\-\{28\}P\-2Fe)\-2 was studied using frequency doubled, Q switched Nd:YAG laser with a 8 ns pulse at 532nm.
应用倍频Nd:YAG脉冲激光,在波长532nm、脉冲宽度为8ns的条件下,研究了金属团簇化合物W2Cu4S6O2(C34H28P2Fe)2的光限幅特性。
6) semi metallized pellet
半金属化球团
1.
The laboratory tests were carried out over the semi metallized pellet under different indurating times,indurating temperatures,coal proportion rates The results had shown that the iron content of the semi metallized pellet could reach to 68% by adopting following parameters:15% bituminous coal,1050?℃ reduction temperature,90?minutes reduction tim
在实验室条件下 ,利用圆盘造球机配制的复合球团 ,进行了不同焙烧温度、不同焙烧时间、不同煤粉配比的半金属化球团试验。
补充资料：金属化纸和金属化薄膜
表面上蒸镀一层很薄 (0.1微米左右)的金属层的纸或薄膜。金属化纸曾应用于电缆、变压器作为屏蔽层,现多用于制造电容器。金属化纸和金属化薄膜的特点是具有自愈性,即当某处击穿时,短路电流使击穿部位周围的金属膜熔化并蒸发而又恢复绝缘性能，因此显著减少纸或薄膜中贯穿性导电疵点和弱点对击穿强度的影响，从而提高工作场强。低压纸介电容器如用铝箔极板（6～7微米）,必须用2～3层纸或薄膜,若用金属化纸或金属化薄膜,只要1层即可,极板的厚度也由6～7微米减少到0.1微米左右，大大节省材料。直流或脉冲电容器用金属化纸时，为了提高绝缘电阻，可以在纸的单面或双面涂以约1微米厚的快干纤维漆，然后在真空中蒸镀0.1微米的金属膜。交流电容器用的金属化纸或金属化薄膜，为了不使介质损耗增大，不喷漆，而是在纸或薄膜表面上直接蒸镀金属膜。用于蒸镀金属膜的金属有锌、镉、镍和铝等，以锌最适合（沸点较低）。有些薄膜（例如聚酯薄膜）可以先在表面上蒸镀银层，然后再蒸镀锌层。
金属化纸或金属化薄膜吸潮后，特别是在较高温度下容易被损伤腐蚀，在储存、加工过程中要采取适当的防潮措施。金属化纸一般不可用氯化物浸渍，以防止纸中析出的氢同氯化物浸渍剂析出的氯作用形成腐蚀性的氯化氢；但加了某些特殊的稳定剂后也可以用氯化物浸渍。
金属化纸或金属化薄膜吸潮后，特别是在较高温度下容易被损伤腐蚀，在储存、加工过程中要采取适当的防潮措施。金属化纸一般不可用氯化物浸渍，以防止纸中析出的氢同氯化物浸渍剂析出的氯作用形成腐蚀性的氯化氢；但加了某些特殊的稳定剂后也可以用氯化物浸渍。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条